1. Hydrogen embrittlement and corrosion behavior of low-temperature carburized austenitic stainless steel
Sammanfattning : For metallic components used in hydrogen environments, hydrogen embrittlement and corrosion have always been important considering potential failure risks. Among many metallic materials, austenitic stainless steel has found broad application because of its excellent corrosion and hydrogen embrittlement resistance. LÄS MER
2. Delayed Hydride Cracking in Irradiated Zircaloy
Sammanfattning : Under some circumstances nuclear fuel cladding tubes made from zirconium based alloys may develop long axial cracks. The formation of these cracks is mainly thought to be connected with the oxiditian and hydriding of the cladding which takes plage after the the formation of a small primary defect. LÄS MER
3. High temperature corrosion of low-alloyed and stainless steels: mechanistic study of chlorine-induced corrosion
Sammanfattning : The global demand on power generation is constantly increasing and so far, also its environmental impact. The environmental impact could primarily be directed to the power generation being based on fossil fuels, giving a net increase of CO2 to the atmosphere when combusted. LÄS MER
4. Laser Based Powder Bed Fusion of Plain Carbon and Low-Alloy Steels: Microstructure and Processability
Sammanfattning : Despite the prominence of laser based powder bed fusion (LB-PBF) as an additive manufacturing technique, the number of alloys that have been approved for the process remains limited. In traditional manufacturing, ferrous alloys are the most common alloy group, consisting primarily of plain carbon and low-alloy steels. LÄS MER
5. Influence of hydrogen on corrosion and stress induced cracking of stainless steel
Sammanfattning : Hydrogen is the smallest element in the periodical table. It has been shown in several studies that hydrogen has a large influence on the corrosion and cracking behaviour of stainless steels. Hydrogen is involved in several of the most common cathode reactions during corrosion and can also cause embrittlement in many stainless steels. LÄS MER