1. 11. Reliability, fatigue and mechanical characterization of lead-free solders for electronic packaging applications

   Författare :Cristina Andersson; Chalmers tekniska högskola; []
   Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; Reliability.; Isothermal mechanical fatigue; Tensile tests; Mechanical behavior; Electronics; Thermal fatigue; Lead-free solders; Low cycle fatigue;

   Sammanfattning : The ever increasing amount of electronic waste, most of which ends up in landfills, has become a serious worldwide concern. In addition to this, the fact that Pb is highly toxic and harmful to humans has lead to the ban of this element from the electronics industry. LÄS MER

3. 12. Failure of thermal barrier coatings under thermal and mechanical fatigue loading : microstructural observations and modelling aspects

   Författare :Håkan Brodin; Anette M. Karlsson; Linköpings universitet; []
   Nyckelord :thermal barrier coating; TBC; delamination; crack initiation; crack propagation; crack growth; oxidation; alumina; spinel; MCrAIY; diffusion; fatigue; modelling; modeling; degradation; TECHNOLOGY; TEKNIKVETENSKAP;

   Sammanfattning : Industrial and air-borne gas turbine hot components suffer from creep, oxidation, corrosion and microstructural degradation if not shielded from the hot and aggressive combustion gases. Two major strategies commercially available are adopted; film cooling by pressurised air and application of protective coatings. LÄS MER

4. 13. Microstructure and Fatigue Analysis of PM-HIPed Alloys : A Focus on Inconel 625 and High-Nitrogen Tool Steel

   Författare :Faezeh Javadzadeh Kalahroudi; Mikael Grehk; Mattias Calmunger; Karlstads universitet; []
   Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; powder metallurgy; hot isostatic pressing; Inconel 625; high-nitrogen tool steel; microstructure; fatigue behavior; inclusions; Materialteknik; Materials Engineering;

   Sammanfattning : Nickel-based superalloys and tool steels are well-known high-performance alloys due to their extensive use in many different industries. Nickel-based superalloys have found their way into aircraft, aerospace, marine, chemical, and petrochemical industries owing to their excellent high-temperature corrosion and oxidation resistance. LÄS MER

5. 14. Alloy Design and Characterization of γ′ Strengthened Nickel-based Superalloys for Additive Manufacturing

   Författare :Jinghao Xu; Johan Moverare; Ru Lin Peng; Eric Jägle; Linköpings universitet; []
   Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; Nickel-based superalloy; Alloy design; Laser powder bed fusion; Cracking susceptibility; Additive manufacturability; Heat treatment; γ′ precipitate; High-temperature mechanical property; Creep.;

   Sammanfattning : Nickel-based superalloys, an alloy system bases on nickel as the matrix element with the addition of up to 10 more alloying elements including chromium, aluminum, cobalt, tungsten, molybdenum, titanium, and so on. Through the development and improvement of nickel-based superalloys in the past century, they are well proved to show excellent performance at the elevated service temperature. LÄS MER

7. 15. Thermal Barrier Coatings : Durability Assessment and Life Prediction

   Författare :Robert Eriksson; Sten Johansson; Michael Schütze; Linköpings universitet; []
   Nyckelord :;

   Sammanfattning : Thermal barrier coating (TBC) systems are coating systems containing a metallic bond coat and a ceramic top coat. TBCs are used in gas turbines for thermal insulation and oxidation resistance. LÄS MER