1. Weld Cracking of Precipitation Hardening Ni-based Superalloys - Investigation of repair welding characteristics and susceptibility towards strain age cracking
Sammanfattning : High temperature resistance and strength requirements make nickel-based superalloys the material of choice for the hot section of aero engines. Fabrication in terms of combining wrought and cast parts in the manufacturing of hot structural components enables component optimisation via the use of wrought high-strength parts, where geometrical constraints allow, and cast parts to produce complex geometries. LÄS MER
2. Cracking during Continuous Casting of Steels : Analysis tools and procedures to identify their causes on microalloyed steel slabs
Sammanfattning : Transverse corner cracks are one of the most common but complex defects formed in microalloyed steels during continuous casting (CC). Such cracks are detrimental because it leads to a loss in productivity with a great impact on environment, energy and economics for several steel making companies all over the world. LÄS MER
3. On the hot crack formation during solidification of iron-base alloys
Sammanfattning : Hot cracking during solidification is a severe problem inmany casting processes, for example in continuous casting.Combinations of low strength and low ductility of the materialat high temperatures and applied tensile stress can cause hotcracking. LÄS MER
4. Alloy Design and Characterization of γ′ Strengthened Nickel-based Superalloys for Additive Manufacturing
Sammanfattning : Nickel-based superalloys, an alloy system bases on nickel as the matrix element with the addition of up to 10 more alloying elements including chromium, aluminum, cobalt, tungsten, molybdenum, titanium, and so on. Through the development and improvement of nickel-based superalloys in the past century, they are well proved to show excellent performance at the elevated service temperature. LÄS MER
5. Powder bed fusion processing of Ni-base superalloys - Defect formation and its mitigation
Sammanfattning : Powder bed fusion of Ni- and Ni-Fe-base superalloys is actively considered a promising manufacturing technology for critical components for the aerospace and industrial gas turbine industries. Such components often operate under harsh conditions, and hence, high demands are placed on both process and feedstock material to meet the strict safety and long-term reliability requirements. LÄS MER