Sökning: "Low cycle fatigue"

Visar resultat 1 - 5 av 71 avhandlingar innehållade orden Low cycle fatigue.

  1. 1. Oxidation, Creep and Fatigue Synergies in Cast Materials for Exhaust Manifolds

    Författare :Shengmei Xiang; Joakim Odqvist; Baohua Zhu; Stefan Jonsson; Johan Ahlström; KTH; []
    Nyckelord :ENGINEERING AND TECHNOLOGY; TEKNIK OCH TEKNOLOGIER; TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; Fatigue; low-cycle fatigue; fatigue in an inert atmosphere; fatigue in a synthetic diesel exhaust atmosphere; corrosion-fatigue; creep-fatigue; high-temperature corrosion; high-temperature fatigue; synergistic effect; corrosion-fatigue synergy; creep-fatigue synergy; high-temperature alloys; fatigue damage; creep-fatigue damage; corrosion-fatigue damage; ductile cast iron; high-alloyed austenitic cast steel; thermal cycling; precipitation; aging.; Materials Science and Engineering; Teknisk materialvetenskap;

    Sammanfattning : The future development of engines of heavy-duty vehicles towards reduced CO2 emission will increase the exhaust gas temperature and render the exhaust atmosphere more corrosive. The current service material of exhaust gas components - a ferritic ductile cast iron called SiMo51 - will soon meet its upper-temperature limit. LÄS MER

  2. 2. On Low-Cycle Fatigue

    Författare :Johan Tryding; Hållfasthetslära; []
    Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY;

    Sammanfattning : The experimental results presented confirm the anticipation that it is extremely important not to confuse the concept of 'static loading' with the one of 'monotonic loading'. In principle three different crack configurations were investigated in: edge-cracks, internal flaws and surface cracks. LÄS MER

  3. 3. Very high cycle fatigue of automotive steels : Testing and computation at 20 kHz

    Författare :Mohamed Sadek; Jens Bergström; Nils Hallbäck; Ulrich Krupp; Karlstads universitet; []
    Nyckelord :ENGINEERING AND TECHNOLOGY; TEKNIK OCH TEKNOLOGIER; Very high cycle fatigue; ultrasonic fatigue testing; automotive steels; fatigue strength; stress intensity computation; crack growth; Materialteknik; Materials Engineering;

    Sammanfattning : Mechanical fatigue failure occurs in components subjected to cyclic loading. A crack initiates at critical regions in the component and propagates during repeated loading. The expected fatigue life depends on the level, type and frequency of the loading. LÄS MER

  4. 4. Low Cycle Fatigue and Thermo-Mechanical Fatigue of Uncoated and Coated Nickel-Base Superalloys

    Författare :Svjetlana Stekovic; Torsten Ericsson; Hael Mughrabi; Linköpings universitet; []
    Nyckelord :ENGINEERING AND TECHNOLOGY; TEKNIK OCH TEKNOLOGIER; AMDRY997; CMSX-4; SCB; Thermo-Mechanical Fatigue; Coatings; Gas Turbine; IC1; IC3; IN792; Low Cycle Fatigue; Nickel-Base Superalloys; RT22; Materials science; Teknisk materialvetenskap;

    Sammanfattning : High strength nickel-base superalloys have been used in turbine blades for many years because of their superior performance at high temperatures. In such environments superalloys have limited oxidation and corrosion resistance and to solve this problem, protective coatings are deposited on the surface. LÄS MER

  5. 5. Comparability of Railway Rail Steels Low Cycle Fatigue Behaviour

    Författare :Martin Schilke; Chalmers University of Technology; []
    Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; railway rail steel; strain energy density; Low cycle fatigue;

    Sammanfattning : Several different kinds of steel are used for railway rails. From simple pearlitic steels for rarely used tracks over premium pearlitic steels for high performance lines to special bainitic, martensitic and austenitic steels for switches and crossings. Most of these steels have been trial and error developed over time in track. LÄS MER