6. Atmospheric Corrosion of Lead. The Influence of Organic acid Vapours and Inorganic Air Pollutants. A contribution Towards Understanding the Environmental Degradation of Historic Organ Pipes
Sammanfattning : This thesis presents different perspectives on the atmospheric corrosion of lead, aiming at a better understanding of the environmental degradation of historical organ pipes. Corroded organ pipes from the field have been analyzed and the environment inside the organ wind system has been mapped. LÄS MER
7. Atmospheric corrosion of Mg and MgAl alloys – characterization and mechanisms
Sammanfattning : The atmospheric corrosion of Mg and MgAl alloys was investigated. Corrosion tests were performed in the laboratory under controlled environment. CP Mg, AM50 and AZ91 samples were exposed at 95% RH and 22°C in the presence and in the absence of 400 ppm CO2 for 24 h to 672 h. The passive film was characterized by means of XPS, FTIR, AES and XRD. LÄS MER
8. Radiation exposure of human populations in villages in Russia and Belarus affected by fallout from the Chernobyl reactor
Sammanfattning : A quarter of a century has elapsed since the catastrophe at the nuclear power plant in Chernobyl. The radioactive fallout affected all the European countries and most severely the three countries of Belarus, Russia and Ukraine. LÄS MER
9. The role of particles on initial atmospheric corrosion of copper and zinc : lateral distribution, secondary spreading and CO2-/SO2-influence
Sammanfattning : The role of sodium chloride (NaCl) particles and ammonium sulfate ((NH4)2SO4) particles on the initial atmospheric corrosion of copper and zinc was investigated under in situ and ex situ conditions using microgravimetry, FTIR spectroscopy, ion chromatography, scanning electron microscopy with x-ray microanalysis and the scanning Kelvin probe. For the first time, in situ infrared spectra were collected on a micron level during particle induced atmospheric corrosion using a recently developed experimental set-up for in situ FTIR microspectroscopy. LÄS MER
10. Initial atmospheric corrosion of copper
Sammanfattning : .... LÄS MER