  1. 1. Atmospheric corrosion of Mg and MgAl alloys – characterization and mechanisms

    Författare :Mehrdad Shahabi Navid; Chalmers tekniska högskola; []
    Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; EDX; CO2; XPS; Mg and MgAl alloys; NaCl; Atmospheric corrosion; Characterization; 3D imaging; SEM; BIB; Thin film; FTIR; XRD; Pitting; Interference microscopy; FIB;

    Sammanfattning : The atmospheric corrosion of Mg and MgAl alloys was investigated. Corrosion tests were performed in the laboratory under controlled environment. CP Mg, AM50 and AZ91 samples were exposed at 95% RH and 22°C in the presence and in the absence of 400 ppm CO2 for 24 h to 672 h. The passive film was characterized by means of XPS, FTIR, AES and XRD. LÄS MER

  3. 2. Atmospheric corrosion of the MgAl alloy AM50 in rheocast and high pressure diecast conditions - Influence of Microstructure, CO2 and NaCl

    Författare :Mehrdad Shahabi Navid; Chalmers tekniska högskola; []
    Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; SEM; MgAl alloy; Atmospheric corrosion; High pressure diecast; XPS; XRD; Rheocast;

    Sammanfattning : The NaCl-induced atmospheric corrosion of the high pressure diecast (HPDC) MgAl alloy AM50 was investigated. Commercially pure (CP) Mg was used as the reference. Two levels of salt; i.e. LÄS MER