36. Thermal cracking of young concrete : partial coefficients, restraint effects and influence of casting joints
Sammanfattning : Cracks can occur due to temperature induced movements during the hardening phase of concrete. Thermal cracks are not decisive for the load-bearing capacity but cause costs for repair and may reduce the life of the structure. The risk of cracking can be judged through safety values, (partial coefficients) given in building codes. LÄS MER
37. On the control of centreline segregation in continous casting
Sammanfattning : .... LÄS MER
38. Exploring expandable microspheres as a novel pore former in gel-cast macroporous alumina
Sammanfattning : Expandable microspheres have been explored as sacrificial templates for the production of macroporous ceramics. Concentrated alumina powder suspensions that contain expandable microspheres have been consolidated by gel-casting. LÄS MER
39. Investigation of Surface Formation in As-Cast and Homogenized 6xxx Aluminium Billets
Sammanfattning : The direct chill (DC) casting technique to produce billets for extrusion and ingots for rollingwas developed in the 1930s. The principle, which is still valid, is a two-stage cooling with a primary cooling at a mould surface followed by water spraying directly on the surface. LÄS MER
40. On the surface quality of continuously cast steels and phosphor bronzes
Sammanfattning : This thesis work concerns about the importance of the cast surfaces, surface phenomenon such as the formation of the oscillation marks and exudation and related defects including cracks and segregation that happened during the continuous casting. All of the investigated materials were collected during the plant trials while an in-depth analysis on these materials was performed at the laboratory scale with certain explanations supported by the schematic and theoretical models. LÄS MER