1. Investigation of Surface Formation in As-Cast and Homogenized 6xxx Aluminium Billets
Sammanfattning : The direct chill (DC) casting technique to produce billets for extrusion and ingots for rollingwas developed in the 1930s. The principle, which is still valid, is a two-stage cooling with a primary cooling at a mould surface followed by water spraying directly on the surface. LÄS MER
2. Direct and indirect magnetocaloric properties of first- and second-order phase transition materials
Sammanfattning : The energy-efficient and environmentally friendly alternative cooling technology based on the magnetocaloric effect (MCE) is discussed in this thesis. The thesis has two major parts, one devoted to material characterization and the other to instrument development. LÄS MER
3. Transformation phenomena in a super duplex stainless steel
Sammanfattning : Duplex stainless steels consist of about equal fractions offerrite and austenite and are attractive due to their highcorrosion resistance against pitting corrosion and stresscorrosion cracking. The pitting corrosion resistance can bedescribed by the PREN value which is defined asPREN=%Cr+3.3*%Mo+16*%N. LÄS MER
4. Reactive Sintering of Cu-Al, Ni-Al and Ni-Ti Powder Mixtures
Sammanfattning : Intermetallic compounds are a distinct group of materials having attractive properties and wide applications. In the present work, the formation of intermetallic compounds from elemental components in Cu-Al, Ni-Al and Ni-Ti systems has been studied. Metallic powders were mixed in stoichiometric ratios corresponding to CuAl2, NiAl and NiTi. LÄS MER
5. Role of alloying elements in Mo5Si3 intermetallics
Sammanfattning : The role of alloying elements in the intermetallic compound Mo5Si3 was studied in the alloying systems Mo5-xMxSi3 (M = Cr, Ti, Nb, Ni, or Co, x = 0.5-2). The effects of the alloying elements were examined by characterising the microstructures and identifying the resulting phases. In the case of Cr and Nb alloying, a solubility of 25% (at. LÄS MER