Sökning: "Hardness"

Visar resultat 11 - 15 av 427 avhandlingar innehållade ordet Hardness.

  1. 11. Acetylation of Solid Wood. Wood Properties and Process Development

    Författare :Pia Larsson Brelid; Chalmers tekniska högskola; []
    Nyckelord :NATURVETENSKAP; NATURAL SCIENCES; microwave heating; deformation; wood; hardness; adhesive bonding; power penetration depth; shear strength; delamination; acetylation; pH; bending strength; dielectric properties; stability;

    Sammanfattning : The influence of acetylation on selected wood properties has been determined for Scandinavian pine and spruce wood, in order to predict the behavior of acetylated wood when it is used in different applications. Only minor differences in both bending strength and the modulus of elasticity were obtained for acetylated wood when compared with unmodified wood, and can, for practical applications, be considered unaltered. LÄS MER

  3. 12. Synthesis and Characterization of Transition Metal Diborides

    Författare :Jimmy Thörnberg; Johanna Rosén; Per Persson; Helmut Riedl; Linköpings universitet; []
    Nyckelord :NATURVETENSKAP; NATURAL SCIENCES; DCMS; HiPIMS; Titanium Diboride; Titanium Aluminum Diboride; Chromium Diboride; Microstructure; Hardness; Oxidation Resistance;

    Sammanfattning : This thesis is devoted towards physical vapor deposition (PVD) of thin films of transition-metal (TM) diborides, focused on the material system TiBx, Ti1-xAlxB2-y and CrBx. The metal diborides are a large family of compounds with both metallic and ceramic properties, due to its bonding nature being a mix of covalent and ionic bonds. LÄS MER

  4. 13. Machinability variations in alloy 718 turbine components

    Författare :Pajazit Avdovic; Chalmers tekniska högskola; []
    Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; variation in tool; hardness; Machining; flank wear; notch wear; alloy 718; grain size; instability; variation in material;

    Sammanfattning : Machinability Variations in Alloy 718 Turbine Components PAJAZIT AVDOVIC Department of Materials and Manufacturing TechnologyChalmers University of Technology AbstractAlloy 718 has a reputation for being very troublesome during the cutting process. It was suspected that this material was too hard and having too fine grain size and that these characteristics caused damage to cutting tools during processing. LÄS MER

  5. 14. On indentation methods for characterization of inelastic materials

    Författare :Susanna Carlsson; KTH; []
    Nyckelord :indentation test; material characterization; hardness; contact area; viscoelasticity; creep; plasticity; friction; residual stress; residual strain; Brinell test; Boussinesq test; Vickers test;

    Sammanfattning : .... LÄS MER

  7. 15. Properties of acetylated solid wood

    Författare :Pia Larsson Brelid; Chalmers tekniska högskola; []
    Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; bending strength; acetylation; shear strength; hardness; deformation; wood; adhesive bonding; delamination; stability; pH;

    Sammanfattning : .... LÄS MER