11. Life Prediction and Mechanical Behavior of Thermal Barrier Coatings
Sammanfattning : Delamination and spallation of thermal barrier coating (TBC) systems, used in hot parts of gas turbines, have been studied with respect to thermal fatigue. TBCs with and without pre-existing cracks were investigated. Thermal shock tests were performed until coating spallation. LÄS MER
12. High-temperature degradation of plasma sprayed thermal barrier coating systems
Sammanfattning : Thermal barrier coating systems (TBCs) are used in gas turbines to prevent high-temperature degradation of metallic materials in the combustor and turbine. One of the main concerns regarding TBCs is poor reliability, and accurate life prediction models are necessary in order to fully utilise the beneficial effects of TBCs. LÄS MER
13. Microstructure and Thermal Conductivity of Liquid Feedstock Plasma Sprayed Thermal Barrier Coatings
Sammanfattning : Thermal barrier coating (TBC) systems are widely used on gas turbine components to provide thermal insulation and oxidation protection. TBCs, incombination with advanced cooling, can enable the gas turbine to operate at significantly higher temperatures even above the melting temperature of the metallic materials. LÄS MER
14. Design of Suspension Plasma Sprayed Thermal Barrier Coatings
Sammanfattning : Thermal barrier coatings (TBCs) are widely used on gas turbine components to provide thermal insulation, which in combination with advanced cooling, can enable the gas turbine to operate at significantly higher temperatures even above the melting temperature of the metallic components. There is a permanent need,mainly due to environmental reasons, to increase the combustion temperature inturbines, hence new TBC solutions are needed. LÄS MER
15. Delamination in APS applied thermal barrier coatings : life modelling
Sammanfattning : Thermal barrier coatings, TBCs, are used in gas turbines as a thermal shield resulting in lower temperature in coated components. The decrease of temperature allows higher gas temperatures in the turbine, which increase the efficiency. LÄS MER