Sökning: "tillväxt av utmattningssprickor"

Hittade 3 avhandlingar innehållade orden tillväxt av utmattningssprickor.

  1. 1. Microstructure and mechanical properties of low-temperature hot isostatic pressed Ti-6Al-4V manufactured by electron beam melting

    Författare :Karthikeyan Thalavai Pandian; Robert Pederson; Thomas Hansson; Magnus Neikter; Högskolan Väst; []
    Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; Additive manufacturing; high-temperature tensile properties; low cycle fatigue; neutron diffraction; fatigue crack growth; Additiv tillverkning; dragprovning vid hög temperatur; låg cykelutmattning; neutrondiffraktion; tillväxt av utmattningssprickor; Production Technology; Produktionsteknik;

    Sammanfattning : Ti-6Al-4V manufactured by electron beam melting Keywords: Additive manufacturing, high-temperature tensile properties, low cycle fatigue, neutron diffraction, fatigue crack growth ISBN: 978-91-89325-27-2 (Printed) 978-91-89325-26-5 (Electronic) Ti-6Al-4V is the most widely used α+β titanium alloy in aerospace engine applications due to its high specific strength. Typically, the alloy is manufactured as castings or forgings and then machined to final geometry. LÄS MER

  3. 2. Numerical Modelling of Short Fatigue Crack Growth

    Författare :Per Hansson; Mekanik; []
    Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; discrete dislocation; Fatigue; grain boundary; short crack;

    Sammanfattning : Fatigue implies repeated loading and unloading of a structure, and components subjected to fatigue might experience nucleation of cracks, and subsequent crack propagation. This might lead to catastrophic consequences, such as complete failure of a structure. LÄS MER

  4. 3. Modelling and simulation of short fatigue cracks

    Författare :Christina Bjerkén; Materialteknik; []
    Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; materialteknik; Materiallära; Material technology; Interface cracks; Dislocations; Short cracks; Local plasticity;

    Sammanfattning : The growth of short fatigue cracks deviates from the behaviour of long fatigue cracks even if subjected to the same nominal driving force. The influence from the microstructure is pronounced, while crack closure effects may not be that important as for longer cracks. LÄS MER