  1. 1. Moisture transport processes in Scots pine - Anomalous capillary suction. Nonisothermal diffusion

    Författare :Ingemar Segerholm; Chalmers tekniska högskola; []
    Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; moisture transport coefficients; nonisothermal; anomalous capillary suction; flux equation; phenomenological approach; wood;

    Sammanfattning : Moisture transport processes in wood have become increasingly important with the growing use of wood as construction material. This thesis deals with two key processes: capillary suction and nonisothermal diffusion. In the study on capillary suction, several methods were used. LÄS MER

  3. 2. Nonisothermal moisture transport in Scots pine : an experimental study of driving potentials and moisture transport coefficients

    Författare :Ingemar Segerholm; Chalmers tekniska högskola; []
    Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY;

    Sammanfattning : .... LÄS MER

  4. 3. Sintering of cemented carbides : experiments and modeling

    Författare :Sven Haglund; KTH; []
    Nyckelord :;

    Sammanfattning : During sintering of cemented carbides large volumetricshrinkage takes place. About half the volume of the originalgreen body is lost during this process. Due to lotal densitydifferentes within the green body undesired shape changes mayalso occur during sintering. LÄS MER

  5. 4. An Experimental Study of Submerged Entry Nozzles (SEN) Focusing on Decarburization and Clogging

    Författare :Arashk Memarpour; Pär Jönsson; Torbjörn Carlberg; KTH; []
    Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; Refractory; SEN; Clogging; REM; Coating; glaze; alkaline; Post- Mortem; industrial preheating; ZrSi2; Graphite; Alumina; Oxidation; Al2O3-C; ZrO2-C; MgO-C; decarburization; reaction mechanism; Yttria Stabilized Zirconia; plasma spray-PVD coating;

    Sammanfattning : The submerged entry nozzle (SEN) is used to transport the molten steel from a tundish to a mould. The main purpose of its usage is to prevent oxygen and nitrogen pick-up by molten steel from the gas. Furthermore, to achieve the desired flow conditions in the mould. LÄS MER