1. Metal Expansion Penetration During Solidification of Grey Cast Iron
Sammanfattning : The meta! expansion penetration has been examined experimentally. The whole casting process was simulated using a commercial software, in order to investigate the solidification characteristics and the pore formation in the casting studied. LÄS MER
2. The mechanisms of metal expansion penetration during solidification of grey cast iron
Sammanfattning : The production of high quality castings requires the casting surface to be clean and free from defects. One type of defect often found is caused by metal penetration into the sand mould. LÄS MER
3. Study of solidification and volume change in lamellar cast iron with respect to defect formation mechanisms
Sammanfattning : Lamellar cast iron is a very important technical alloy and the most used material in the casting production, and especially in the automotive industry which is the major consumer. Beside the many great properties, it is inclined to form casting defects of which some can be prevented, and some may be repaired subsequently. LÄS MER
4. Alloy element redistribution during sintering of powder metallurgy steels
Sammanfattning : Homogenization of alloying elements is desired during sintering of powder metallurgy components. The redistribution processes such as penetration of liquid phase into the interparticle/grain boundaries of solid particles and subsequent solid-state diffusion of alloy element(s) in the base powder, are important for the effective homogenization of alloy element(s) during liquid phase sintering of the mixed powders. LÄS MER
5. Study of microstructure development in hypoeutectic grey cast iron
Sammanfattning : The avoidance of shrinkage porosity and metal expansion penetration defects as well as the control of the size and number of eutectic colonies and the tensile properties of the casting are issues of major importance in the production of lamellar cast iron. These defects, characteristics and properties are related to the microstructure that develops during solidification. LÄS MER