Sökning: "casting temperature"

Visar resultat 1 - 5 av 98 avhandlingar innehållade orden casting temperature.

  1. 1. The mechanisms of metal expansion penetration during solidification of grey cast iron

    Författare :Izudin Dugic; Preben Norgaard Hansén; Linköpings universitet; []
    Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; Grey cast iron; solidification; solidification modelling; graphite expansion; molar volume; casting simulation; thermal analysis; thermoanalysis cup; casting temperature; inoculation; inoculant; metal expansion penetration; eutectic cell size; primary austenite; austenite grain; TECHNOLOGY; TEKNIKVETENSKAP;

    Sammanfattning : The production of high quality castings requires the casting surface to be clean and free from defects. One type of defect often found is caused by metal penetration into the sand mould. LÄS MER

  3. 2. Metal Expansion Penetration During Solidification of Grey Cast Iron

    Författare :Izudin Dugic; Linköpings universitet; []
    Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; Grey cast iron; solidification; solidification modelling; graphite expansion; molar volume; casting simulation; thennal analysis; thermoanalysis cup; casting temperature; inoculation; inoculant; meta! expansion penetration; eutectic cell size.; TECHNOLOGY; TEKNIKVETENSKAP;

    Sammanfattning : The meta! expansion penetration has been examined experimentally. The whole casting process was simulated using a commercial software, in order to investigate the solidification characteristics and the pore formation in the casting studied. LÄS MER

  4. 3. The effect of microstructure and temperature on the atmospheric corrosion of Mg-Al alloys

    Författare :Mohsen Esmaily; Chalmers tekniska högskola; []
    Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; Atmospheric corrosion; microstructure; temperature; corrosion product; magnesium;

    Sammanfattning : The NaCl-induced atmospheric corrosion behavior of the Mg-Al alloy AM50 produced by rheo-casting (RC) and high pressure die casting (HPDC) techniques was studied in the laboratory. The exposures were performed at 95% RH in the absence and presence of 400 ppm CO2 at 22, 4 and -4ºC. In parallel, 99.97%Mg was investigated as reference. LÄS MER

  5. 4. Cracking during Continuous Casting of Steels : Analysis tools and procedures to identify their causes on microalloyed steel slabs

    Författare :Rosa Maria Pineda Huitron; Esa Vuorinen; Pavel Ernesto Ramí­rez López; Maria Begoña Santillana; Luleå tekniska universitet; []
    Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; Transverse corner cracks; Continuous Casting; Microalloyes steels; Secondary cooling; Cooling curves; Crack susceptibility; Materialteknik; Engineering Materials;

    Sammanfattning : Transverse corner cracks are one of the most common but complex defects formed in microalloyed steels during continuous casting (CC). Such cracks are detrimental because it leads to a loss in productivity with a great impact on environment, energy and economics for several steel making companies all over the world. LÄS MER

  7. 5. Al-Si Cast Alloys - Microstructure and Mechanical Properties at Ambient and Elevated Temperature

    Författare :Mohammadreza Zamani; Anders Jarfors; Sten Johansson; Jönköping University; []
    Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; Al-Si based casting alloys; elevated temperature; microstructural scale effect; Sr modification;

    Sammanfattning : Aluminium alloys with Si as the major alloying element form a class of material providing the most significant part of all casting manufactured materials. These alloys have a wide range of applications in the automotive and aerospace industries due to an excellent combination of castability and mechanical properties, as well as good corrosion resistance and wear resistivity. LÄS MER