Sökning: "GMAW"

Visar resultat 1 - 5 av 6 avhandlingar innehållade ordet GMAW.

  1. 1. Experimental study on cold lap formation in tandem gas metal arc welding

    Författare :Peigang Li; Lars-Erik Svensson; Leif Karlsson; []
    Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; GMAW; Cold lap; oxide; Tandem arc welding; Manufacturing and materials engineering; Produktions- och materialteknik;

    Sammanfattning : .... LÄS MER

  2. 2. A Framework for optimised welding of fatigue loaded structures Applied to gas metal arc welding of fillet welds

    Detta är en avhandling från Trollhättan : University West

    Författare :Erik Åstrand; Gunnar Bolmsjö; Fredrik Sikström; Heikki Remes; [2016]
    Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; GMAW; Fatigue; Welding procedures; Fillet welds; Weld quality; Production Technology; Produktionsteknik; Manufacturing and materials engineering; Produktions- och materialteknik;

    Sammanfattning : Welding is a key process for heavy steel structures, but it is also a weak link in the structure since fatigue fractures in welds are a common cause of failure. This thesis proposes several changes in order to improve the fatigue properties in acost effective way, enabling reduced weight and reduced cost of welded structures. LÄS MER

  3. 3. Welding of Heavy Structures Subjected to Fatigue

    Detta är en avhandling från Trollhättan : University West

    Författare :Erik Åstrand; [2013]
    Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; Weld quality; Fillet welds; Weld procedures; Fatigue; Welded applications.; GMAW;

    Sammanfattning : Welding is a key process for heavy steel structures, but it is also a weak link of the structure since fatigue fractures in welds are a common cause for failures. This thesis proposes several changes in order to improve the fatigue properties in a cost effective way. LÄS MER

  4. 4. Experimental Study on Cold Lap Formation in Tandem Gas Metal Arc Welding

    Detta är en avhandling från Trollhättan : University West

    Författare :Peigang Li; [2011]
    Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; oxides; imperfection; spatter; silicon; lack of fusion; overflow; temperature energy; overlap; cold lap; manganese; tandem GMAW;

    Sammanfattning : Tandem gas metal arc welding (GMAW) is a high productivity welding process which is appliedin many industries. However, a type of imperfection, known as cold lap, was revealed thatmostly accompanies the tandem GMAW process. LÄS MER

  5. 5. Cold lap formation in Gas Metal Arc Welding of steel An experimental study of micro-lack of fusion defects

    Detta är en avhandling från Trollhättan : University West

    Författare :Peigang Li; Lars-Erik Svensson; Norbert Enzinger; [2013]
    Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; Tandem GMAW; old laps; lack of fusion; Spatter; Overlap; Overflow; Manganese; Silicon; Oxides; Temperature; Manufacturing and materials engineering; Produktions- och materialteknik;

    Sammanfattning : Cold laps are defined as micro-lack of fusion defects at the weld toe more or less parallel to the surface of the parent plate. These defects are known to negatively influence the fatigue properties of weldments. Previous studies suggest that cold lap formation can not be avoided completely in Gas Metal Arc Welding (GMAW). LÄS MER