36. Iron losses during desulphurisation of hot metal
Sammanfattning : After injection of calcium carbide and magnesium during desulphurisation of hot metal, the slag is normally solid and contains large amounts of iron. Besides the enclosed iron droplets in the slag, drawn-off hot metal during slag skimming also accounts for iron losses during desulphurisation of hot metal. LÄS MER
37. Some aspects of hydrogen reduction of iron ore
Sammanfattning : Fines of hematite and magnetite were studied in the fluidized bed using a pure hydrogen atmosphere in the temperature range of 768 to 888 K. Hematite pellets were studied based on Thermogravimetric Analysis (TGA) experiments using hydrogen atmospheres containing 0–15 % pH2O, in the temperature range of 873 to 1173 K. LÄS MER
38. Numerical Modeling of Plasticity in FCC Crystalline Materials Using Discrete Dislocation Dynamics
Sammanfattning : Plasticity in crystalline solids is controlled by the microscopic line defects known as “dislocations”. Decisive role of dislocations in crystal plasticity in addition to fundamentals of plastic deformation are presented in the current thesis work. LÄS MER
39. Martensitic Transformation in High Carbon Steels - Martensite Tetragonality and Impact of Cooling Rate
Sammanfattning : Case-hardened gears are an essential part of our every day life in their role of power transmission in cars and heavy-duty trucks. The increasing use of low pressure carburizing (LPC) for case-hardening in combination with high pressure gas quenching (HPGQ) for cooling opens new possibilities in the design of heat treatments for improved fatigue performance. LÄS MER
40. Microstructure and Inclusion Characteristics in Steels with Ti-oxide and TiN Additions
Sammanfattning : Non-metallic inclusions in steels are generally considered to be detrimental for mechanical properties. However, it has been recognized that certain inclusions, such as Ti-oxide and TiN, can serve as potent nucleation sites for the formation of intragranular ferrite (IGF) in low-alloy steels. LÄS MER