High-Temperature Durability Prediction of Ferritic-Martensitic Steel

Sammanfattning: Materials used for high-temperature steam turbine sections are generally subjected to harsh environments with temperatures up to 625 °C. The superior creep resistance of 9–12 % Cr ferritic-martensitic steels makes them desirable for those critical steam turbine components. Additionally, the demand for fast and frequent steam turbine start-ups, i.e. flexible operations, causes accelerated fatigue damage in critical locations, such as grooves and notches, at the high-temperature inner steam turbine casing. A durability assessment is necessary to understand the material behaviour under such high temperatures and repeated loading, and it is essential for life prediction. An accurate and less conservative fatigue life prediction approach is achieved by going past the crack initiation stage and allowing controlled growth of cracks within safe limits. Besides, beneficial load-temperature history effects, i.e. warm pre-stressing, must be utilised to enhance the fracture resistance to cracks. This dissertation presents the high-temperature durability assessment of FB2 steel, a 9-12 % Cr ferritic-martensitic steam turbine steel.Initially, isothermal low-cycle fatigue testing was performed on FB2 steel samples. A fatigue life model based on finite element strain range partitioning was utilised to predict fatigue life within the crack initiation phase. Two fatigue damage regimes were identified, i.e. plastic- and creep-dominated damage, and the transition between them depended on temperature and applied total strain. Cyclic deformation and stress relaxation behaviour were investigated to produce an elastic-plastic and creep material model that predicts the initial and mid-life cyclic behaviour of the FB2 steel.Furthermore, the thermomechanical fatigue crack growth behaviour of FB2 steel was studied. Crack closure behaviour was observed and accounted for numerically and experimentally, where crack growth rate curves collapsed into a single curve. Interestingly, the collapsed crack growth curves coincided with isothermal crack growth tests performed at the minimum temperature of the thermomechanical crack growth tests. In addition, hold times and changes in the minimum temperature of the thermomechanical fatigue cycle did not influence crack closure behaviour.Finally, warm pre-stressing effects were explored for FB2 steel. A numerical prediction model was produced to predict the increase in the apparent fracture toughness. Warm pre-stressing effects can benefit the turbine life by enhancing fracture resistance and allowing longer fatigue cracks to grow within safe limits.