Sökning: "hydrogen embrittlement"

Visar resultat 11 - 15 av 16 avhandlingar innehållade orden hydrogen embrittlement.

  1. 11. Phase-field modeling of stress-induced precipitation and kinetics in engineering metals

    Författare :Claudio F. Nigro; Christina Bjerkén; Ylva Mellbin; Pär A T Olsson; Reinhart Pippan; Malmö universitet; []
    Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; phase-field theory; finite element method; corrosion; finite volume method; phase transformation; hydride; hydrogen embrittlement; linear elastic fracture mechanics;

    Sammanfattning : The formation of brittle compounds in metals operating in corrosive environments can be a tremendous source of embrittlement for industrial structures and such phenomenon is commonly enhanced in presence of stresses. To study this type of microstructural change modeling is preferred to experiment to reduce costs and prevent undesirable environmental impacts. LÄS MER

  3. 12. A Fracture Mechanics Approach to Study Hydrogen Embrittlement in High Strength Martensitic Steels

    Författare :Armin E. Halilović; Pål Efsing; Jonas Faleskog; Carl F.O. Dahlberg; Covadonga Betegon; KTH; []
    Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; Solid Mechanics; Hållfasthetslära;

    Sammanfattning : High strength steels that are subjected to hydrogen experience embrittlement where the mechanical properties are reduced, and premature failure of components may occur. Although the phenomenon has been recognized for over 150 years, it is not clear what drives embrittlement. LÄS MER

  4. 13. Linear and Nonlinear Mechanics of Lattice Materials : Computational Modelling and Experiments

    Författare :Danial Molavitabrizi; Mahmoud Mousavi; Kristofer Gamstedt; Haiyang Yu; Samuel Forest; Uppsala universitet; []
    Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; Teknisk fysik med inriktning mot tillämpad mekanik; Engineering science with specialization in Applied Mechanics;

    Sammanfattning : Lattice materials are artificial materials made of repeating unit-cells. The internal architecture of these materials can be engineered for a specific application such as energy absorption, heat transfer, or acoustic damping. LÄS MER

  5. 14. Deterioration of Polyethylene Exposed to Chlorinated Species in Aqueous Phases : Test Methods, Antioxidants Consumption and Polymer Degradation

    Författare :Wenbin Yu; Ulf Gedde; Sahar Al-Malaika; KTH; []
    Nyckelord :Antioxidants; Polyethylene pipes; Chlorine dioxide; Degradation;

    Sammanfattning : This thesis presents a study of antioxidant depletion in water containing chlorinated species (water containing 10 ppm either Cl2 or ClO2, buffered to pH = 6.8), the degradation products in the aqueous phase, and polyethylene pipe degradation scenarios. LÄS MER

  7. 15. An Experimental Study to Understand the Localized Corrosion and Environment-Assisted Cracking Behavior of AISI 420-Martensitic Stainless Steel

    Författare :Krishnan Hariramabadran Anantha; Jinshan Pan; Robert Akid; KTH; []
    Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; Kemi; Chemistry;

    Sammanfattning : Motivation and aim: Currently steel molds are designed with cooling channels to reduce the solidification time of molten plastic within the mold to improve the productivity. As water is generally used as the cooling medium, corrosion and environment-assisted cracking (EAC) leading towards the dysfunction of mold, can increase the production downtime. LÄS MER