6. Hydrogen embrittlement and corrosion behavior of low-temperature carburized austenitic stainless steel
Sammanfattning : For metallic components used in hydrogen environments, hydrogen embrittlement and corrosion have always been important considering potential failure risks. Among many metallic materials, austenitic stainless steel has found broad application because of its excellent corrosion and hydrogen embrittlement resistance. LÄS MER
7. Effect of water contamination on the diffused content of hydrogen under stress in AISI-52100 bearing steel
Sammanfattning : Abstract Hydrogen embrittlement is a degradation process of mechanical/tribological properties (toughness, wear etc.) of mating steel surfaces. This is caused by the presence and interaction of hydrogen with applied stresses. Therefore, it is important to quantify the hydrogen content which could be dissolved under applied stresses in steel. LÄS MER
8. Inconel 718 and Hydrogen
Sammanfattning : The nickel based superalloy IN718 is known to be sensitive to hydrogen, causing degradation of its mechanical properties. The degrading mechanism commonly proposed is based on an increased mobility and density of dislocations, caused by the dissolved hydrogen. This results in a decreased yield stress and a premature fracture. LÄS MER
9. Phase field modeling of flaw-induced hydride precipitation kinetics in metals
Sammanfattning : Hydrogen embrittlement can manifest itself as hydride formation in structures when in contact with hydrogen-rich environments, e.g. in space and nuclear power applications. To supplant experimentation, modeling of such phenomena is beneficial to make life prediction reduce cost and increase the understanding. LÄS MER
10. Designing metallic glasses : Alloying, properties, and degrees of freedom
Sammanfattning : The present design rules for metallic glasses with respect to glass formation, thermal stability (resistance to crystallisation), and material properties can still be improved. A main design rule is to use thermodynamic calculations to determine the composition of eutectic points in the phase space. LÄS MER