  1. 1. Very high cycle fatigue of automotive steels : Testing and computation at 20 kHz

    Författare :Mohamed Sadek; Jens Bergström; Nils Hallbäck; Ulrich Krupp; Karlstads universitet; []
    Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; Very high cycle fatigue; ultrasonic fatigue testing; automotive steels; fatigue strength; stress intensity computation; crack growth; Materialteknik; Materials Engineering;

    Sammanfattning : Mechanical fatigue failure occurs in components subjected to cyclic loading. A crack initiates at critical regions in the component and propagates during repeated loading. The expected fatigue life depends on the level, type and frequency of the loading. LÄS MER

  3. 2. The effect of inelastic deformation on crack loading

    Författare :Dimosthenis Floros; Chalmers tekniska högskola; []
    Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; Numerical simulation; Mixed mode; Configurational mechanics; Gradient plasticity;

    Sammanfattning : Rolling contact fatigue (RCF) cracks in rails are among the most detrimental railway track defects, in relation to reliability and cost. The cracks grow in a mixed mode II & III, which in combination with the rotating stress field in the neighborhood of the crack-tip, large plastic deformations on the rail surface, crack face friction due to the compressive stresses from the wheel load and anisotropic crack growth resistance, add to the complexity related to the study of RCF cracks. LÄS MER

  4. 3. Finite element procedures for crack path prediction in multi-axial fatigue

    Författare :Dimosthenis Floros; Chalmers tekniska högskola; []
    Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; Fracture mechanics; Configurational forces; Mixed-mode; Numerical simulation; Rolling contact fatigue; Plasticity;

    Sammanfattning : Rolling Contact Fatigue (RCF) cracks in rails are among the most detrimental railway track defects regarding reliability and cost. The cracks typically grow in shear mode up to a certain length at which they might arrest or kink into a more tensile-driven growth. LÄS MER