Sökning: "solidification rate"

Visar resultat 1 - 5 av 56 avhandlingar innehållade orden solidification rate.

  1. 1. Compacted graphite iron : On solidification phenomena related to shrinkage defects

    Författare :Björn Domeij; Attila Diószegi; Babette Tonn; Jönköping University; []
    Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; Compacted graphite iron; Spheroidal graphite iron; Solidification; Microsegregation; Porosity; Kompaktgrafitjärn; segjärn; stelning; mikrosegregation; porositet;

    Sammanfattning : An improved understanding of solidification of compacted graphite iron (CGI) is necessary to predict shrinkage related casting defects. Spheroidal graphite is not only found in ductile iron (SGI) but usually also in CGI, but its characteristics and role in this material is less understood. LÄS MER

  3. 2. Microstructures and properties of powder metallurgy high alloy steels

    Författare :Jinhua Wang; Chalmers tekniska högskola; []
    Nyckelord :NATURVETENSKAP; NATURAL SCIENCES; phase constitution; SEM; HIPing; EDS; SIMS; microstructure; martensite; high speed steel; atomization; cooling rate; austenite; floating densitometry; stainless steel; carbide; ferrite; materials technology; pressing; compacting; powder metallugry; sintering; solidification; composition; DTA;

    Sammanfattning : .... LÄS MER

  4. 3. On the hot crack formation during solidification of iron-base alloys

    Författare :Karin Hansson; KTH; []
    Nyckelord :hot cracking; hot tearing; cracking fracturing ; tearing; ductility; brittleness; embrittlement; fractures; ductile brittle transition; solidification; iron; copper; nickel; Invar; steels; free machining steels; stainless steels; penetration; crack;

    Sammanfattning : Hot cracking during solidification is a severe problem inmany casting processes, for example in continuous casting.Combinations of low strength and low ductility of the materialat high temperatures and applied tensile stress can cause hotcracking. LÄS MER

  5. 4. Rapid solidification behaviour of Fe and Al based alloys

    Författare :Sathees Ranganathan; Hasse Fredriksson; Zhongyun Fan; KTH; []
    Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; Rapid solidification; Melt spinning; Metastable phases; Fe based alloys.; Metallurgical process and manufacturing engineering; Metallurgisk process- och produktionsteknik;

    Sammanfattning : Rapid solidification experiment on Fe-Cr-Mo-Mn-Si-C alloy was performed to investigate metastable phases formed during the solidification. A wide range of cooling rate was used to analyse the sample from melt spinning technique (~107 K/s) to water quenching method (~102 K/s). LÄS MER

  7. 5. An Experimental Study of Liquid Steel Sampling

    Författare :Ola Ericsson; Pär Jönsson; Andrey Karasev; Malin Hallberg; KTH; []
    Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; liquid steel sampling; slag protection; filling velocity; solidification rate; sample homogeneity; Metallurgical process and manufacturing engineering; Metallurgisk process- och produktionsteknik;

    Sammanfattning : Sampling of liquid steel to control the steel making process is very important in the steel industry. However, there are numerous types of disposable samplers and no united standard for sampling. The goal in this study is to investigate the effect of slag protection type and sample geometry on sampling parameters and sample homogeneity. LÄS MER