  1. 16. Corrosion Behavior of HVAF-Sprayed Bi-Layer Coatings

    Författare :Esmaeil Sadeghimeresht; Nicolaie Markocsan; Per Nylén; Högskolan Väst; []
    Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; Thermal spray coating; HVAF; Corrosion protection; Galvanic corrosion; Composition; Microstructure; EIS; Polarization; OCP; Production Technology; Produktionsteknik; Manufacturing and materials engineering; Produktions- och materialteknik;

    Sammanfattning : In a variety of engineering applications, components are subjected to corrosive environment. Protective coatings are essential to improve the functional performances and/or extend the lifetime of the components. LÄS MER

  3. 17. Failure of thermal barrier coatings under thermal and mechanical fatigue loading : microstructural observations and modelling aspects

    Författare :Håkan Brodin; Anette M. Karlsson; Linköpings universitet; []
    Nyckelord :thermal barrier coating; TBC; delamination; crack initiation; crack propagation; crack growth; oxidation; alumina; spinel; MCrAIY; diffusion; fatigue; modelling; modeling; degradation; TECHNOLOGY; TEKNIKVETENSKAP;

    Sammanfattning : Industrial and air-borne gas turbine hot components suffer from creep, oxidation, corrosion and microstructural degradation if not shielded from the hot and aggressive combustion gases. Two major strategies commercially available are adopted; film cooling by pressurised air and application of protective coatings. LÄS MER

  4. 18. The rule of hydrogen and rare earth metals in the formation of protective metal-oxides

    Författare :Bent N. Tveten; KTH; []
    Nyckelord :chromium; high-temperature corrosion; oxide growth; scale adherence; hydrogen; yttria; REM; reactive element effect; gas phase analysis;

    Sammanfattning : The effects of hydrogen and rare earth metal (REM) additionson the oxidation behavior of metals and alloys that formchromia, alumina and zirconia in 20 mbar O2and/or H2O have been investigated at elevated temperatures.The metal-gas reactions were studied by the use of isotopicallylabeled gas in combination with mass spectrometry and bymeasuring changes in the total pressure in a closed reactionchamber. LÄS MER

  5. 19. Ni-based coatings for high temperature corrosion protection

    Författare :Esmaeil Sadeghimeresht; Shrikant V. Joshi; Nicolaie Markocsan; Petri Vuoristo; Högskolan Väst; []
    Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; Thermal Spray Coating; HVAF; High Temperature Corrosion Protection; Composition; Microstructure; Dispersed Oxide; Production Technology; Produktionsteknik; Manufacturing and materials engineering; Produktions- och materialteknik;

    Sammanfattning : Biomass/waste-fired boilers severely suffer from high temperature corrosion of critical load-bearing components, e.g. water-wall and superheater tubes, due to presence of Cl-containing corrosive species. LÄS MER

  7. 20. Oxidation behaviour of MCrAlX coatings : effect of surface treatment and an Al-activity based life criterion

    Författare :Pimin Zhang; Ru Lin Peng; Xin-Hai Li; Sten Johansson; Fang Liu; Linköpings universitet; []
    Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY;

    Sammanfattning : MCrAlY coatings (M=Ni and/or Co) have been widely used for the protection of superalloy components against oxidation and hot corrosion in the hot sections of gas turbines. The drive to improve engine combustion efficiency while reducing emissions by increasing the operation temperature brings a big challenge for coating design. LÄS MER