1. Chloride initiated reinforcement corrosion in marine concrete
Sammanfattning : Factors affecting the total chloride threshold for initiation of pitting corrosion in reinforced concrete were investigated by means of field and laboratory exposure tests. Factors affecting the chloride penetration into concrete were also investigated by means of field tests. The thesis consists of a summary (86 p.) and 11 papers attached. LÄS MER
2. Environmental Actions and Response - Reinforced Concrete Structures exposed in Road and Marine Environments
Sammanfattning : The expenses for repair, maintenance and remediation of existing concrete structures have significantly increased. A large proportion of these expenses are due to problems related to a lacking durability of the structure. LÄS MER
3. Chloride profiling in marine concrete - methods and tools for sampling
Sammanfattning : This project focuses on how to determine the chloride content in concrete structures exposed to marine environment in an accurate way. When analyzing dust from dry drilling in concrete, it is very often a fact that the chloride profiles show extensive variations even if the sampling has been performed within a very concentrated area with the sampling points close to each other. LÄS MER
4. Environmental actions on concrete exposed in marine and road environments and its response - Consequences for the initiation of chloride induced reinforcement corrosion
Sammanfattning : The object of the study presented here has been to describe, further explain and model the influence of the exposure conditions on reinforced concrete structures and the consequences on their expected service life. The focus has been on investigating and quantifying the exposure conditions for structures in marine and road conditions exposed to chloride ions. LÄS MER
5. Microbial biofilm communities associated with degradation of sprayed concrete in subsea tunnels
Sammanfattning : Deterioration of concrete leads to reduced structural strength implying high societal challenge with huge economic impact. In the Oslofjord subsea tunnel, complex microbial biofilm activity together with abiotic attack from saline groundwater are responsible for concrete matrix degradation and steel fiber corrosion. LÄS MER