  1. 1. Key Aspects of Sintering Powder Metallurgy Steel Prealloyed with Chromium and Manganese

    Författare :Ola Bergman; Chalmers tekniska högskola; []
    Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; Manganese; Prealloyed; Sintering; Mechanical properties; Chromium; Spinel oxide; Powder metallurgy; PM steel; Oxide reduction; Residual oxides; Atmosphere;

    Sammanfattning : The powder metallurgy (PM) process is a cost efficient near net-shape technology suitable for sustainable manufacturing of structural steel components. A drawback with the PM technology is the difficulty to use oxidation sensitive alloying elements, such as Cr and Mn. LÄS MER

  3. 2. Welds in the lean duplex stainless steel LDX 2101 : effect of microstructure and weld oxides on corrosion properties

    Författare :Elin M. Westin; John Ågren; KTH; []
    Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; Duplex stainless steel; welding; weld metal; HAZ; nitrogen; manganese; austenite formation; phase balance; precipitates; pitting resistance; heat input; solidification; element loss; evaporation; deposition; weld oxides; discoloration; mechanical properties; thermo-mechanical simulation; Geeble; GTA; laser; LOM; SEM; EDS; TEM; Leco; EPMA; ferroxyl test; XPS; post weld cleaning; pickling; Materials science; Teknisk materialvetenskap;

    Sammanfattning : Duplex stainless steels are a very attractive alternative to austenitic grades due to their higher strength and good corrosion performance. The austenitic grades can often be welded autogenously, while the duplex grades normally require addition of filler metal. LÄS MER

  4. 3. Microstructure and properties of welds in the lean duplex stainless steel LDX 2101

    Författare :Elin M. Westin; John Ågren; Hannu Hänninen; KTH; []
    Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; Duplex stainless steel; welding; HAZ; nitrogen; manganese; microstructure; austenite formation; phase balance; precipitates; element distribution; segregation; depletion; solidification; pitting corrosion resistance; solidification; element loss; evaporation; deposition; weld oxide; thermo-mechanical simulation; thermodynamic modelling; EPMA; XPS; post-weld cleaning; pickling; Metallurgical process and manufacturing engineering; Metallurgisk process- och produktionsteknik;

    Sammanfattning : Duplex stainless steels can be very attractive alternatives to austenitic grades due to their almost double strength at equal pitting corrosion resistance. When welding, the duplex alloys normally require addition of filler metal, while the commodity austenitic grades can often be welded autogenously. LÄS MER

  5. 4. Anisotropic fatigue properties of engineering steel : a microstructural characterisation

    Författare :Jonas Höijer; Chalmers tekniska högskola; []
    Nyckelord :NATURVETENSKAP; NATURAL SCIENCES; microstructure; fractography; LOM; SIMS; manganese sulphide morphology; fatigue; case hardening steel; Anisotropy; SEM; forging; through hardening steel;

    Sammanfattning : .... LÄS MER

  7. 5. Fatigue Anisotropy in Forged Components

    Författare :Cornelius Temmel; Chalmers tekniska högskola; []
    Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; Inclusion Cluster; Low Sulfur; Machinability; Inclusion; Manganese Sulfide; Quenching Crack; Forging; Isotropic Quality; Steel; Anisotropy;

    Sammanfattning : Ever-growing requirements on combustion engine efficiency of motor vehicles demand increasing service loads in powertrain components. Optimization of component material is therefore inevitable. A major detriment with many forged transmission components is their anisotropic mechanical behavior, not least during cyclic loading. LÄS MER