  1. 1. Welds in the lean duplex stainless steel LDX 2101 : effect of microstructure and weld oxides on corrosion properties

    Författare :Elin M. Westin; John Ågren; KTH; []
    Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; Duplex stainless steel; welding; weld metal; HAZ; nitrogen; manganese; austenite formation; phase balance; precipitates; pitting resistance; heat input; solidification; element loss; evaporation; deposition; weld oxides; discoloration; mechanical properties; thermo-mechanical simulation; Geeble; GTA; laser; LOM; SEM; EDS; TEM; Leco; EPMA; ferroxyl test; XPS; post weld cleaning; pickling; Materials science; Teknisk materialvetenskap;

    Sammanfattning : Duplex stainless steels are a very attractive alternative to austenitic grades due to their higher strength and good corrosion performance. The austenitic grades can often be welded autogenously, while the duplex grades normally require addition of filler metal. LÄS MER

  3. 2. Microstructure and properties of welds in the lean duplex stainless steel LDX 2101

    Författare :Elin M. Westin; John Ågren; Hannu Hänninen; KTH; []
    Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; Duplex stainless steel; welding; HAZ; nitrogen; manganese; microstructure; austenite formation; phase balance; precipitates; element distribution; segregation; depletion; solidification; pitting corrosion resistance; solidification; element loss; evaporation; deposition; weld oxide; thermo-mechanical simulation; thermodynamic modelling; EPMA; XPS; post-weld cleaning; pickling; Metallurgical process and manufacturing engineering; Metallurgisk process- och produktionsteknik;

    Sammanfattning : Duplex stainless steels can be very attractive alternatives to austenitic grades due to their almost double strength at equal pitting corrosion resistance. When welding, the duplex alloys normally require addition of filler metal, while the commodity austenitic grades can often be welded autogenously. LÄS MER