1. Low Cycle Fatigue and Thermo-Mechanical Fatigue of Uncoated and Coated Nickel-Base Superalloys
Sammanfattning : High strength nickel-base superalloys have been used in turbine blades for many years because of their superior performance at high temperatures. In such environments superalloys have limited oxidation and corrosion resistance and to solve this problem, protective coatings are deposited on the surface. LÄS MER
2. Aspects of creep-fatigue in gas turbine hot parts
Sammanfattning : The goal is reliable creep-fatigue lifing methodology for industrial gas turbines.A literature study on high temperature materials used in gas turbines reveals that:• Most testing/modelling work has focused on characterisation and modelling of material response in isothermal standard tests, i.e. creep, tensile and LCF tests. LÄS MER
3. Constitutive modeling of a nickel base superalloy : with a focus on gas turbine applications
Sammanfattning : Gas turbines are used where large amounts of energy is needed, typically as engines in aircraft, ferries and power plants. From an efficiency point of view it is desirable to increase the service temperature as much as possible. LÄS MER
4. Thermal and Mechanical Behaviors of High Temperature Coatings
Sammanfattning : With superior oxidation and corrosion resistance, metallic coatings (i.e. diffusion coatings and MCrAlX coatings) are widely used to protect hot components made of superalloys in turbine engines. LÄS MER
5. Performance of High-temperature Coatings : Oxidation and Interdiffusion
Sammanfattning : The use of aluminiferous coatings profoundly improves the service life of superalloys but leads to the microstructural degradation of superalloys and thus the loss of mechanical properties. To solve this trade-off, two strategies were employed in this research. LÄS MER