  1. 6. Metal Expansion Penetration During Solidification of Grey Cast Iron

    Författare :Izudin Dugic; Linköpings universitet; []
    Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; Grey cast iron; solidification; solidification modelling; graphite expansion; molar volume; casting simulation; thennal analysis; thermoanalysis cup; casting temperature; inoculation; inoculant; meta! expansion penetration; eutectic cell size.; TECHNOLOGY; TEKNIKVETENSKAP;

    Sammanfattning : The meta! expansion penetration has been examined experimentally. The whole casting process was simulated using a commercial software, in order to investigate the solidification characteristics and the pore formation in the casting studied. LÄS MER

  3. 7. Factors Related to the Formation of Gas Porosity in Grey Cast Iron: Investigation of Core Gas Evolution and Gas Concentrations in Molten Iron

    Författare :Jessica Orlenius; Chalmers tekniska högskola; []
    Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; core binders; Gas porosity; hydrogen; grey iron; gas absorption; nitrogen; oxygen; gas evolution rate; green sand; mould filling; gas volume; gas solubility;

    Sammanfattning : Since gas porosity is a major casting problem, it is of greatest importance to increase the knowledge about the foundry process in order to minimise the presence of gas porosity and thereby improving the casting quality. Gas porosity is generally considered to originate from gases precipitated during solidification of iron and from entrained gas picked up by the metal during the mould filling. LÄS MER

  4. 8. The mechanisms of metal expansion penetration during solidification of grey cast iron

    Författare :Izudin Dugic; Preben Norgaard Hansén; Linköpings universitet; []
    Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; Grey cast iron; solidification; solidification modelling; graphite expansion; molar volume; casting simulation; thermal analysis; thermoanalysis cup; casting temperature; inoculation; inoculant; metal expansion penetration; eutectic cell size; primary austenite; austenite grain; TECHNOLOGY; TEKNIKVETENSKAP;

    Sammanfattning : The production of high quality castings requires the casting surface to be clean and free from defects. One type of defect often found is caused by metal penetration into the sand mould. LÄS MER

  5. 9. Elastoplasticity of Grey Cast Iron FE-Algorithms and Biaxial Experiments

    Författare :Hans E. Hjelm; Chalmers tekniska högskola; []
    Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; Biaxial experiments; multiaxial elastoplastic behaviour; graphite flakes; FE-codes; hardening behaviour; graphitic grey cast iron;

    Sammanfattning : This thesis focuses on multiaxial elastoplastic behaviour of graphitic grey cast iron with the aim to provide physically appropriate and numerically reliable constitutive relations for use in FE-codes. To achieve this goal, this work is divided into three parts: Biaxial experiments are performed on thin cruciform specimens. LÄS MER

  7. 10. Varved lake sediments and diagenetic processes

    Författare :Veronika Gälman; Ingemar Renberg; Daniel Conley; Umeå universitet; []
    Nyckelord :NATURVETENSKAP; NATURAL SCIENCES; Varved annually laminated lake sediment; diagenesis; varve appearance; iron; sulfur; chemical speciation; iron cycling; carbon; nitrogen; stabile isotopes; δ13C; δ15N; Earth sciences; Geovetenskap;

    Sammanfattning : Varved (annually laminated) sediments are of great interest for inference of past environmental conditions, as they provide dated records with high time resolution. After deposition, the sediment varves are affected by diagenesis; i.e., chemical, physical and biological changes that occur within the sediment. LÄS MER