  1. 1. Degradation Mechanisms of Heat Resistant Steel at Elevated Temperatures : In an Iron Ore Pelletizing Industry

    Författare :Erik A. A. Nilsson; Marta-Lena Antti; Ragnar Tegman; Jan-Erik Svensson; Luleå tekniska universitet; []
    Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; stainless steel; Grate-Kiln; microstructure; corrosion; as-casted; thermal cycling; erosion; deposition; Engineering Materials; Materialteknik;

    Sammanfattning : This thesis focuses on the different degradation mechanisms of the stainless steel in a travelling grate in a Grate-Kiln iron ore pellet indurator. The travelling grate is a conveyor belt that transports green-body pellets to a rotary kiln while the pellets are being dried and pre-heated to a temperature of 900-1100 °C by recycled hot air. LÄS MER

  3. 2. High Temperature Corrosion in Fluidised Bed Environment

    Författare :Anna Nafari; Chalmers tekniska högskola; []
    Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; CFB; coatings; Ni and iron based alloys; HCl; SO2; loop seal; High temperature corrosion; erosion corrosion test rig; surface characterization and temperature gradient;

    Sammanfattning : Successful material selection for power plants is the result of understanding the environment in each boiler. The boiler environment is affected by fuel chemistry, co-firing, process control and deposits as well as boiler type, design, size and load. LÄS MER

  4. 3. Oxide Formation and Degradation during Erosion-Corrosion of Iron and Nickel Based Alloys

    Författare :Rikard Norling; Chalmers tekniska högskola; []
    Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; AES; fluidised bed; FBC; XPS; erosion-corrosion; SO2; crack formation; surface analysis; HCl; enhanced oxidation;

    Sammanfattning : Erosion-corrosion is, in many technical applications, a serious material degradation process caused by dynamic particle/fluid mixtures. Pipes transporting particle containing liquids, jet engines, gas turbines, and fluidised bed combustion (FBC) power plants are examples of systems which are considered to be especially susceptible. LÄS MER

  5. 4. Erosion - Corrosion Resistance and Adhesion of Laser and Thermally Deposited Coatings in Fluidised Beds

    Författare :Anders Hjörnhede; Chalmers tekniska högskola; []
    Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; coating; fluidised bed; HVOF; laser cladding; CFB; FBC; adhesion testing; PFBC; thermal spraying; arc spray; erosion - corrosion; acoustic emission;

    Sammanfattning : High temperature erosion - corrosion is the major source for degradation of components such as heat exchangers, tubes, cyclones and water walls used in Fluidised Bed Combustion (FBC) plants. By coating the exposed components with a protective material, the degradation rate can be decreased. LÄS MER