  1. 1. Durability of Reinforced Concrete under Impressed Current Cathodic Protection

    Författare :Emma Zhang; Chalmers tekniska högskola; []
    Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; durability; cathodic protection and prevention; anode system; service life; critical chloride content; Chloride initiated corrosion;

    Sammanfattning : Impressed current cathodic protection (ICCP) and prevention (ICCPre) are reliable and efficient techniques to stop, control and postpone corrosion in reinforced concrete structures. However, the wide application of this technique has been limited by the high cost of the anode system. LÄS MER

  3. 2. Chloride Induced Corrosion of Reinforcement Steel in Concrete - Threshold Values and Ion Distributions at the Concrete-Steel Interface

    Författare :Nelson Dias Ferreira Da Silva; Chalmers tekniska högskola; []
    Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; LA-ICP-MS; pitting corrosion; chloride threshold values; concrete-steel interface;

    Sammanfattning : The chloride threshold value (Cth), or critical chloride content, is defined as the chloride concentration at the depth of the reinforcement, which initiates the depassivation of steel in concrete. However, very limited information is available regarding the chloride distributions at the interface with the steel. LÄS MER

  4. 3. Possibilities to use industrial oxidic by-products as neutralising agent in bioleaching and the effect of chloride on biooxidation

    Författare :Chandra Sekhar Gahan; S. Subramanian; Luleå tekniska universitet; []
    Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; Process Metallurgy; Processmetallurgi;

    Sammanfattning : The cost for neutralisation is the second largest cost in a bioleaching operation for which, possibilities to replace generally used lime/limestone was tested. Industrial oxidic by-products generated form Swedish industries were investigated for neutralising capacities by chemical leaching with sulphuric acid at pH 1. LÄS MER

  5. 4. Water and alkali salts in the hydrating and hardened green cement-based materials: Hydration process, moisture content and transport

    Författare :Liming Huang; Chalmers tekniska högskola; []
    Nyckelord :NATURVETENSKAP; NATURAL SCIENCES; TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; NATURVETENSKAP; NATURAL SCIENCES; TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; Formation factor; Electrical conductivity; Moisture transport; Pore structure; Sustainable cement-based materials; Hydration; Alkali salts; Supplementary cementitious materials;

    Sammanfattning : Reducing CO2 emissions in the production of cementitious binder is the most effective way to decrease the environmental impact of the construction industry, so a large amount of supplementary cementitious materials (SCMs) has been used in the green concrete. Both the SCMs and alkali salts in binders influence the hydration process and the structure in hardened cement-based materials. LÄS MER

  7. 5. Redistribution of moisture and ions in cement based materials

    Författare :Magnus Åhs; Avdelningen för Byggnadsmaterial; []
    Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; Moisture redistribution; ion redistribution; cement based materials; hysteresis; sorption isotherm; scanning;

    Sammanfattning : There were two principal objectives for this thesis. The first was to develop a methodology and evaluation model of moisture redistribution in order to make the future relative humidity in a screeded concrete slab predictable. The second objective was to develop a method to determine the critical humidity for ion transport in concrete. LÄS MER