11. Plastic Shrinkage Cracking In Concrete : Mitigation and Modelling
Sammanfattning : Early-age (up to 24 hours after casting) cracking may become problematic in any concrete structure. It can have a negative influence on the aesthetics of the concrete structure, as well as decreasing the durability and serviceability by facilitating the ingress of harmful materials into the concrete bulk. LÄS MER
12. On the hot crack formation during solidification of iron-base alloys
Sammanfattning : Hot cracking during solidification is a severe problem inmany casting processes, for example in continuous casting.Combinations of low strength and low ductility of the materialat high temperatures and applied tensile stress can cause hotcracking. LÄS MER
13. Thermal cracking of young concrete : partial coefficients, restraint effects and influence of casting joints
Sammanfattning : Cracks can occur due to temperature induced movements during the hardening phase of concrete. Thermal cracks are not decisive for the load-bearing capacity but cause costs for repair and may reduce the life of the structure. The risk of cracking can be judged through safety values, (partial coefficients) given in building codes. LÄS MER
14. On folding of coated papers
Sammanfattning : The mechanical behaviour of coated papers during folding has been investigated. This problem has been studied with experimental techniques and numerical analyses in order to give a better understanding of the folding properties of coated papers pertinent to the mechanical behaviour in general, and particularly cracking along the fold. LÄS MER
15. In-plane tension behaviour of masonry
Sammanfattning : The main purpose of the present work is to increase knowledge of in-plane tension behav-iour of masonry and develop a model able to describe the impact of parameters influencing cracking caused by restrained shrinkage. In the process the mechanism of load transfer between units and mortar joints is described. LÄS MER