Sökning: "crack growth"

Visar resultat 16 - 20 av 184 avhandlingar innehållade orden crack growth.

1. 16. Fatigue crack growth under complex loading

   Författare :Mats Yngvesson; KTH; []
   Nyckelord :;

   Sammanfattning : .... LÄS MER

3. 17. Numerical simulation of crack growth and wear in rails

   Författare :Jim Brouzoulis; Chalmers tekniska högskola; []
   Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; crack propagation; material forces; Rolling Contact Fatigue; wear; railway mechanics;

   Sammanfattning : Wear and rolling contact fatigue (RCF) of rails are huge problems for the railway industry with increased world-wide occurrence during the last decades. It is, therefore, of high interest to develop tools for the prediction of wear and RCF which can be used to estimate rail life. LÄS MER

4. 18. Growth of fatigue cracks subjected to non-proportional Mode I and II

   Författare :Peter Dahlin; Mårten Olsson; Veronique École; KTH; []
   Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; Fatigue crack growth; Mode II overloading; Crack closure; Sequential mixed mode loading; Other engineering mechanics; Övrig teknisk mekanik;

   Sammanfattning : This thesis deals with some aspects of crack growth in the presence of cyclic loading, i.e. fatigue. The cyclic load cases studied here are primary of non-proportional mixed mode type. LÄS MER

5. 19. On initiation of chemically assisted crack growth and crack propagation paths of branching cracks in polycarbonate

   Författare :Ulf Hejman; Malmö högskola; []
   Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; stress corrosion; crack initiation; multiple cracking; polycarbonate; three point bending; stress corrosion cracking; polycarbonate; dissolution; branching; experiment; finite element modelling; stress corrosion; crack initiation; multiple cracking; polycarbonate; three point bending; branching.;

   Sammanfattning : Stress corrosion, SC, in some cases gives rise to stress corrosion cracking, SCC, which differs from purely stress intensity driven cracks in many aspects. They initiate and grow under the influence of an aggressive environment in a stressed substrate. They grow at low load and may branch. LÄS MER

7. 20. Fatigue of Spot Welded Joints: Experiments and Life Predictions

   Författare :Hans-Fredrik Henrysson; Chalmers tekniska högskola; []
   Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; crack closure; crack propagation; crack initiation; finite element method; damage accumulation; variable amplitude; fracture mechanics; fatigue; spot welds;

   Sammanfattning : Methods to assess the fatigue strength of spot welds in built-up structures are used on a daily basis in the automotive industry. Efficient and reliable numerical methods make it possible to achieve designs with low weight, low manufacturing costs and good durability within short development cycles, since the number of prototypes built can be reduced. LÄS MER