  1. 1. Crack growth in single crystal gas turbine blade alloys under service-like conditions

    Författare :Frans Palmert; Johan Moverare; David Gustafsson; Mikael Segersäll; Philippa A.S. Reed; Linköpings universitet; []
    Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; Single crystal superalloy; TMF; Crack growth; Crystallographic crack growth; Aging; Hold time; Creep crack growth;

    Sammanfattning : This work concerns the fatigue crack growth behaviour of nickel base single crystal superalloys. The main industrial application of this class of materials is in gas turbine blades, where the ability to withstand severe mechanical loading in combination with high temperatures is required. LÄS MER

  3. 2. High Strain Fatigue Crack Growth and Crack Closure

    Författare :Michael Andersson; Materialteknik; []
    Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; materialteknik; Materiallära; Material technology; crack closure; high strain fatigue; crack grotwh;

    Sammanfattning : Understanding of the growth of fatigue cracks is of utmost importance since such growth often has a profound influence on the life of components subjected to cyclic loading. Thus, reliable fatigue life models enable a more efficient use of materials and improve the performance and efficiency in many applications. LÄS MER

  4. 3. Crack growth paths in rolling contact fatigue — Numerical predictions

    Författare :Mohammad Salahi Nezhad; Chalmers tekniska högskola; []
    Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; Vector crack tip displacement; Crack face friction; Crack growth direction; Crack propagation; Rolling contact fatigue;

    Sammanfattning : Rolling contact fatigue (RCF) cracks in railway wheels and rails are costly and complex to deal with. Despite the extensive research efforts that have been put into understanding the mechanisms and developing appropriate predictive models for RCF crack growth, there are still a lot of open questions. LÄS MER

  5. 4. Numerical models of ductile crack growth

    Författare :Annika Trädegård; KTH; []
    Nyckelord :solid mechanics; nonlinear fracture mechanics; elastic-plastic fracture; finite element method; remeshing; constraint; two-parameter characterisation; stable ductile crack growth; cleavage; weibull stress; void growth;

    Sammanfattning : .... LÄS MER

  7. 5. Oxygen Induced High Temperature Crack Growth in Ni-base Superalloys

    Författare :Leif Viskari; Chalmers tekniska högskola; []
    Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; Diffusion; Environmental influence; Crack growth; Atom probe tomography; Electron Microscopy; Deformation; Crack tip oxidation; Hold-time fatigue;

    Sammanfattning : Oxygen induced crack growth is a serious concern for the performance of Ni-base superalloys. These alloys are used in gas-turbine engines where they are exposed to hightemperatures, mechanical loads and oxygen-rich environments. LÄS MER