16. Anisotropy in pearlitic steel subjected to rolling contact fatigue - modelling and experiments
Sammanfattning : In rails and wheels subjected to severe rolling/sliding contact, large plastic deformations accumulate in the surface layer. This decreases the fatigue resistance of components and makes this layer prone to formation of common rolling contact related defects. LÄS MER
17. Influence of thermal loading on mechanical properties of railway wheel steels
Sammanfattning : Material integrity and properties of wheels are critical in railway traffic, as wheels fulfil the important function of transferring load and traction from the vehicle to the rail track. Steels with a pearlitic microstructure are commonly used for wheels due to their height strength, low cost and good wear properties. LÄS MER
18. A study on wear characteristics of high strength steels under sliding contact
Sammanfattning : In the last decades, significant improvements regarding the design, materials and technology of rock drills have been made. Likewise, in sheet metal forming, forming tools experience very high contact pressures when processing high strength steel sheets. LÄS MER
19. On the modeling of anisotropy in pearlitic steel subjected to rolling contact fatigue
Sammanfattning : One of the main sources of damage caused by Rolling Contact Fatigue (RCF) inrailway components is the large plastic deformations that accumulate in the surface layerof these components. Large plastic deformations in components made of pearlitic steelinduce anisotropy in the mechanical properties of the material. LÄS MER
20. Low Cycle Fatigue and Thermo-Mechanical Fatigue of Uncoated and Coated Nickel-Base Superalloys
Sammanfattning : High strength nickel-base superalloys have been used in turbine blades for many years because of their superior performance at high temperatures. In such environments superalloys have limited oxidation and corrosion resistance and to solve this problem, protective coatings are deposited on the surface. LÄS MER