1. Growth and Heat Treatment Studies of Al-Cr-O and Al-Cr-O-N Thin Films
Sammanfattning : Aluminum oxide based thin films are applied on cutting tool inserts as a top layer to protect the underlying nitride or carbide functional layer from the harsh working environment in terms of abrasive and chemical wear under thermal and pressure load. This Thesis explores the synthesis and characterization of the next generations of multifunctional wear-resistant thin film coatings in the form of Al-Cr-O and Al-Cr-O-N compounds. LÄS MER
2. Super duplex stainless steels : Microstructure and propertiesof physically simulated base and weld metal
Sammanfattning : High-temperature processing and application of super duplex stainless steel(SDSS) are associated with the risk of changes in the ferrite/austenite balance and precipitation of secondary phases. This study was therefore aimed at improving knowledge about effects of thermal cycles on the microstructure and properties of SDSS base and weld metal. LÄS MER
3. Evaluation of Non-Metallic Inclusions after Deformation and Their Effect on the Machinability of Steel
Sammanfattning : The presence of non-metallic inclusions (NMIs) have critical effects on both the mechanical properties and machinability of steels. In the present thesis, one focus is to study the characteristics of deformed sulfides (MnS) for a stainless steel (3R65) and a tool steel (42CrMo4). LÄS MER
4. Influence of multiple welding cycles on microstructure and corrosion resistance of a super duplex stainless steel
Sammanfattning : Super duplex stainless steel (SDSS) has found a wide use in demanding applications such as offshore, chemical and petrochemical industries thanks to its excellent combination of mechanical properties and corrosion resistance. Welding of SDSS, however, is associated with the risk of precipitation of secondary phases and formation of excessive amounts of ferrite in the weld metal and heat affected zone. LÄS MER
5. Rapid solidification behaviour of Fe and Al based alloys
Sammanfattning : Rapid solidification experiment on Fe-Cr-Mo-Mn-Si-C alloy was performed to investigate metastable phases formed during the solidification. A wide range of cooling rate was used to analyse the sample from melt spinning technique (~107 K/s) to water quenching method (~102 K/s). LÄS MER