1. 6. Design of Thermal Barrier Coatings

   Författare :Nicholas Curry; Nicolaie Markocsan; Per Nylén; Matthias Oechsner; Högskolan Väst; []
   Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; Industrial Gas Turbine; Aero Turbine; Thermal Barrier Coating; Atmospheric Plasma Spraying; Suspension Plasma Spraying; Thermal Conductivity; Thermo-cyclic fatigue; Thermal Shock; Manufacturing and materials engineering; Produktions- och materialteknik;

   Sammanfattning : Thermal barrier coatings (TBC’s) are used to provide both thermal insulation and oxidation protection to high temperature components within gas turbines. The development of turbines for power generation and aviation has led to designs where the operation conditions exceed the upper limits of most conventional engineering materials. LÄS MER

3. 7. Failure of thermal barrier coatings under thermal and mechanical fatigue loading : microstructural observations and modelling aspects

   Författare :Håkan Brodin; Anette M. Karlsson; Linköpings universitet; []
   Nyckelord :thermal barrier coating; TBC; delamination; crack initiation; crack propagation; crack growth; oxidation; alumina; spinel; MCrAIY; diffusion; fatigue; modelling; modeling; degradation; TECHNOLOGY; TEKNIKVETENSKAP;

   Sammanfattning : Industrial and air-borne gas turbine hot components suffer from creep, oxidation, corrosion and microstructural degradation if not shielded from the hot and aggressive combustion gases. Two major strategies commercially available are adopted; film cooling by pressurised air and application of protective coatings. LÄS MER