  1. 1. In-situ phase studies of the Zr-H system

    Författare :Tuerdi Maimaitiyili; Malmö högskola; []
    Nyckelord :Zirconium hydride; synchrotron X-ray diffraction; neutron diffraction; phase transformation; in-situ hydrogen charging; hydrogen related degradation; in situ phase transformation; hydrogen embrittlement; hydrogen charging; zirconium hydride; γ-ZrH; hydrogen induced degradation;

    Sammanfattning : Zirconium alloys are widely used in the nuclear industry because of their high strength, good corrosion resistance and low neutron absorption cross-section. However, zirconium has strong affinity for hydrogen, which may lead to hydrogen concentration build-up over time during a corrosion reaction when exposed to water. LÄS MER

  2. 2. Phase transformation and stability studies of the Zr-H system

    Författare :Tuerdi Maimaitiyili; Lars Hallstadius; Malmö högskola; []
    Nyckelord :Zirconium hydride; synchrotron X-ray diffraction; Nuclear materials; phase transformation; in-situ hydrogen charging; hydrogen related degradation; neutron diffraction; powder diffraction; Rietveld analysis; γ-ZrH; hydrogen embrittlement; zirconium hydride; hydrogen charging; in situ phase transformation; hydrogen induced degradation;

    Sammanfattning : Zirconium alloys are widely used in the nuclear industry because of their high strength, good corrosion resistance and low neutron absorption cross-section. Zirconium has a strong affinity for hydrogen, however, and if hydrogen concentration builds up, the material will gradually degrade. LÄS MER