  1. 21. Mechanical and Environmental Durability of High Performance Bio-based Composites

    Författare :Newsha Doroudgarian; Egidija Rainosalo; Luleå tekniska universitet; []
    Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; Polymera konstruktionsmaterial; Polymeric Composite Materials;

    Sammanfattning : This study is an initial step within the on-going project on development of high performance bio-based composites with improved mechanical (fatigue) and environmental (elevated humidity and temperature) durability. In the presented thesis the performance of cellulosic fibers (flax and regenerated cellulose), bio-based resins (Tribest, EpoBioX, Palapreg, and Envirez) and their composites under exposure to elevated humidity has been studied. LÄS MER

  3. 22. Mechanics of microdamage development and stiffness degradation in fiber composites

    Författare :Johannes Eitzenberger; Luleå tekniska universitet; []
    Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; Polymeric Composite Materials; Polymera konstruktionsmaterial;

    Sammanfattning : Damage in composites reduces its performance and durability and thus its usefulness. The common subject in all papers presented in the licentiate thesis is distributed microdamage, and the materials of interest are a Hemp/Lignin natural composite and glass/carbon fiber reinforced plastics composites. LÄS MER

  4. 23. Effect of light power density variation on dental light-cure resin composites

    Författare :Nazanin Emami; Luleå tekniska universitet; []
    Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; Machine Elements; Maskinelement; Polymeric Composite Materials; Polymera konstruktionsmaterial;

    Sammanfattning : Dental resin based composites are tooth-colored filling materials composed of synthetic resins and particulate ceramic reinforcing filler particles. The resin system also contains molecules that promote and/or modify the polymerisation reaction of the dimethacrylate resin monomers. LÄS MER

  5. 24. Variables affecting stress development and resin conversion in light-cured dental composites

    Författare :Nazanin Emami; Luleå tekniska universitet; []
    Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; Machine Elements; Maskinelement; Polymeric Composite Materials; Polymera konstruktionsmaterial;

    Sammanfattning : The general aim of this dissertation was to identify and investigate factors that can be used to minimize stress development in light cured dental resins without compromising the conversion level of the polymer. Modulus of elasticity, polymerization contraction strain, degree of conversion and shrinkage of light-cure dental composites were determined after curing with three different light power densities where total irradiated energy (J/cm2) kept constant. LÄS MER

  7. 25. Fiber bridging concepts applied to short fiber composites

    Författare :Patrik Fernberg; Luleå tekniska universitet; []
    Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; Polymera konstruktionsmaterial; Polymeric Composite Materials;

    Sammanfattning : Polymer composite materials are in wide-spread use in the transportation industry. In aerospace industry the use these materials are established while in automotive industry the interest is increasing. LÄS MER