  1. 1. Aluminide Diffusion Coatings for Ni Based Superalloys. Coating and Oxide Microstructure

    Författare :Johan Angenete; Chalmers University of Technology; []
    Nyckelord :microstructure; aluminide diffusion coatings; nickel based superalloys; SEM; TEM; high temperature oxidation;

    Sammanfattning : This thesis reports on investigations of high temperature oxidation resistant aluminide diffusion coatings for Ni based superalloys. Such coatings basically consist of a .BETA.-NiAl layer at the surface of the . LÄS MER

  2. 2. Reactive Sintering of Cu-Al, Ni-Al and Ni-Ti Powder Mixtures

    Författare :Hossein Sina; Materialteknik; []
    Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; Sintering; In-situ microscopy; DSC; Intermetallic; aluminide;

    Sammanfattning : Intermetallic compounds are a distinct group of materials having attractive properties and wide applications. In the present work, the formation of intermetallic compounds from elemental components in Cu-Al, Ni-Al and Ni-Ti systems has been studied. Metallic powders were mixed in stoichiometric ratios corresponding to CuAl2, NiAl and NiTi. LÄS MER

  3. 3. A Ni3Al-alloy and its Composites as Potential Wear Resistant Materials for Advanced Applications

    Författare :Karin Anne Xia Gong; Chalmers University of Technology; []
    Nyckelord :Abrasive wear; Intermetallic matrix composite; Friction coefficient; Wear-resistant materials.; Nickel aluminide; Specific wear rate; Sliding wear;

    Sammanfattning : The Ni3Al-based intermetallic alloys as engineering materials in service, they may be subjected to a wear environment of some sort. Hence, it is technologically important to understand the tribological response and to determine methodologies to improve wear resistance of these advanced materials. LÄS MER

  4. 4. Microstructure of Pt modified aluminide diffusion coatings on Ni based single crystal superalloys

    Författare :Johan Angenete; Chalmers University of Technology; []
    Nyckelord :SEM; microstructure; platinum modified aluminide diffusion coatings; nickel based superalloys; high temperature oxidation; EDS; TEM;

    Sammanfattning : .... LÄS MER

  5. 5. Low Cycle Fatigue and Thermo-Mechanical Fatigue of Uncoated and Coated Nickel-Base Superalloys

    Författare :Svjetlana Stekovic; Torsten Ericsson; Hael Mughrabi; Linköpings universitet; []
    Nyckelord :ENGINEERING AND TECHNOLOGY; TEKNIK OCH TEKNOLOGIER; AMDRY997; CMSX-4; SCB; Thermo-Mechanical Fatigue; Coatings; Gas Turbine; IC1; IC3; IN792; Low Cycle Fatigue; Nickel-Base Superalloys; RT22; Materials science; Teknisk materialvetenskap;

    Sammanfattning : High strength nickel-base superalloys have been used in turbine blades for many years because of their superior performance at high temperatures. In such environments superalloys have limited oxidation and corrosion resistance and to solve this problem, protective coatings are deposited on the surface. LÄS MER