1. Experimental and modelling studies of sulphide capacities of some silicate and aluminate melts
Sammanfattning : .... LÄS MER
2. Sulphide capacities of mulicomponent slags
Sammanfattning : In the present thesis, experimental measurements have beencarried out to determine the sulphide capacities of the binaryslags Al2O3-MnO, "FeO"-SiO2, "FeO"-CaO, "FeO"-MnO, ternary slags Al2O3-MgO-SiO2, Al2O3-MnO-SiO2, Al2O3-CaO-MgO, MgO-MnO-SiO2, Al2O3-MgO-MnO,"FeO"-Al2O3-SiO2, "FeO"-CaO-SiO2, "FeO"-MgO-SiO2, "FeO"-MnO-SiO2,quatenary slags Al2O3-CaO-MgO-MnO, Al2O3- CaO-MgO-SiO2,Al2O3-CaO-MnO-SiO2, CaO-MgO-MnO-SiO2, quinary slag Al2O3-CaO-MgO-MnO-SiO2, and the six component slag "FeO"-Al2O3-CaO-MgO-MnO-SiO2.The technique used was to bring the melt to equilibrium witha gas mixturecontaining Ar-CO-CO2-SO2. LÄS MER
3. Measurements of the thermodynamic activities of chromium and vanadium oxides in CaO-MgO-Al2O3-SiO2 slags
Sammanfattning : In the present work, the thermodynamic activities of chromium and vanadium oxide in CaO-SiO2-MgO-Al2O3 slags were measured using gas-slag equilibration technique. The slag was equilibrated with a gas mixture of CO, CO2 and Ar gases enabling well-defined oxygen partial pressures in the gas mixture (PO2=10-3,10-4,10-5 Pa) at temperatures 1803, 1823K, 1873, 1923 K. LÄS MER
4. A Study of EAF Austenitic and Duplex Stainless Steelmaking Slags Characteristics
Sammanfattning : The high temperature microstructure of the solid phases within the electric arc furnace (EAF) slag has a large effect on the process features such as foamability of the slag, chromium recovery, consumption of the ferroalloys and the wear rate of the refractory. The knowledge of the microstructural and compositional evolution of the slag phases during the EAF process stages is necessary for a good slag praxis. LÄS MER