Sökning: "Lower bainite"

Hittade 3 avhandlingar innehållade orden Lower bainite.

  1. 1. Formation of Bainite in Steels

    Författare :Jiaqing Yin; Annika Borgenstam; Bevis Hutchinson; KTH; []
    Nyckelord :ENGINEERING AND TECHNOLOGY; TEKNIK OCH TEKNOLOGIER; TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; Fe-C alloys; Bainitic transformation; Proeutectoid ferrite; Upper bainite; Lower bainite; Morphology; Steels.; Materials Science and Engineering; Teknisk materialvetenskap;

    Sammanfattning : A systematic survey of morphology of bainite and proeutectoid ferrite was carried out in order to validate some old thoughts of bainite transformation mechanism. It is confirmed that there is no morphological evidence supporting a sharp change neither between Widmanstätten ferrite and the ferritic component of upper bainite, nor between upper and lower bainite. LÄS MER

  2. 2. Effect of Microstructure on Mechanical Properties of High Strength Steel Weld Metalsn

    Författare :Enda Keehan; Chalmers University of Technology; []
    Nyckelord :strength; bainite; carbon; TEM; dilatometry; microstructure; impact toughness; neural network modelling; martensite; manganese; FEGSEM; nickel;

    Sammanfattning : The effects of variations in alloying content on the microstructure and mechanical properties of high strength steel weld metals have been studied. Based on neural network modelling, weld metals were produced using shielded metal arc welding with nickel at 7 or 9 wt. %, manganese at 2 or 0.5 wt. LÄS MER

  3. 3. Effect of austenitising temperature and cooling rate on microstructures of hot-work tool steels

    Författare :María Teresa Coll Ferrari; Leif Karlsson; Hans-Olof Andrén; Högskolan Väst; []
    Nyckelord :ENGINEERING AND TECHNOLOGY; TEKNIK OCH TEKNOLOGIER; TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; Tool steel; Heat Treatment; Austenitising Temperature; Large Tools; Tempering Carbides; Bainitic Microstructures; Production Technology; Produktionsteknik; Manufacturing and materials engineering; Produktions- och materialteknik;

    Sammanfattning : The average size of hot-work tools has gradually increased over the past years.This affects the effective temperature cycle tools experience during hardening,as large dimensions prevent uniform and rapid cooling, and thereby the resulting microstructures and properties. LÄS MER