1. 1. Oxidation, Creep and Fatigue Synergies in Cast Materials for Exhaust Manifolds

   Författare :Shengmei Xiang; Joakim Odqvist; Baohua Zhu; Stefan Jonsson; Johan Ahlström; KTH; []
   Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; Fatigue; low-cycle fatigue; fatigue in an inert atmosphere; fatigue in a synthetic diesel exhaust atmosphere; corrosion-fatigue; creep-fatigue; high-temperature corrosion; high-temperature fatigue; synergistic effect; corrosion-fatigue synergy; creep-fatigue synergy; high-temperature alloys; fatigue damage; creep-fatigue damage; corrosion-fatigue damage; ductile cast iron; high-alloyed austenitic cast steel; thermal cycling; precipitation; aging.; Teknisk materialvetenskap; Materials Science and Engineering;

   Sammanfattning : The future development of engines of heavy-duty vehicles towards reduced CO2 emission will increase the exhaust gas temperature and render the exhaust atmosphere more corrosive. The current service material of exhaust gas components - a ferritic ductile cast iron called SiMo51 - will soon meet its upper-temperature limit. LÄS MER

3. 2. High Strain Fatigue Crack Growth and Crack Closure

   Författare :Michael Andersson; Materialteknik; []
   Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; materialteknik; Materiallära; Material technology; crack closure; high strain fatigue; crack grotwh;

   Sammanfattning : Understanding of the growth of fatigue cracks is of utmost importance since such growth often has a profound influence on the life of components subjected to cyclic loading. Thus, reliable fatigue life models enable a more efficient use of materials and improve the performance and efficiency in many applications. LÄS MER

4. 3. Crack growth paths in rolling contact fatigue — Numerical predictions

   Författare :Mohammad Salahi Nezhad; Chalmers tekniska högskola; []
   Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; Vector crack tip displacement; Crack face friction; Crack growth direction; Crack propagation; Rolling contact fatigue;

   Sammanfattning : Rolling contact fatigue (RCF) cracks in railway wheels and rails are costly and complex to deal with. Despite the extensive research efforts that have been put into understanding the mechanisms and developing appropriate predictive models for RCF crack growth, there are still a lot of open questions. LÄS MER

5. 4. Numerical Modelling of Short Fatigue Crack Growth

   Författare :Per Hansson; Mekanik; []
   Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; discrete dislocation; Fatigue; grain boundary; short crack;

   Sammanfattning : Fatigue implies repeated loading and unloading of a structure, and components subjected to fatigue might experience nucleation of cracks, and subsequent crack propagation. This might lead to catastrophic consequences, such as complete failure of a structure. LÄS MER

7. 5. Failure of thermal barrier coatings under thermal and mechanical fatigue loading : microstructural observations and modelling aspects

   Författare :Håkan Brodin; Anette M. Karlsson; Linköpings universitet; []
   Nyckelord :thermal barrier coating; TBC; delamination; crack initiation; crack propagation; crack growth; oxidation; alumina; spinel; MCrAIY; diffusion; fatigue; modelling; modeling; degradation; TECHNOLOGY; TEKNIKVETENSKAP;

   Sammanfattning : Industrial and air-borne gas turbine hot components suffer from creep, oxidation, corrosion and microstructural degradation if not shielded from the hot and aggressive combustion gases. Two major strategies commercially available are adopted; film cooling by pressurised air and application of protective coatings. LÄS MER