  1. 1. On the hot crack formation during solidification of iron-base alloys

    Författare :Karin Hansson; KTH; []
    Nyckelord :hot cracking; hot tearing; cracking fracturing ; tearing; ductility; brittleness; embrittlement; fractures; ductile brittle transition; solidification; iron; copper; nickel; Invar; steels; free machining steels; stainless steels; penetration; crack;

    Sammanfattning : Hot cracking during solidification is a severe problem inmany casting processes, for example in continuous casting.Combinations of low strength and low ductility of the materialat high temperatures and applied tensile stress can cause hotcracking. LÄS MER

  3. 2. Oxygen Induced High Temperature Crack Growth in Ni-base Superalloys

    Författare :Leif Viskari; Chalmers tekniska högskola; []
    Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; Diffusion; Environmental influence; Crack growth; Atom probe tomography; Electron Microscopy; Deformation; Crack tip oxidation; Hold-time fatigue;

    Sammanfattning : Oxygen induced crack growth is a serious concern for the performance of Ni-base superalloys. These alloys are used in gas-turbine engines where they are exposed to hightemperatures, mechanical loads and oxygen-rich environments. LÄS MER

  4. 3. Cracking during Continuous Casting of Steels : Analysis tools and procedures to identify their causes on microalloyed steel slabs

    Författare :Rosa Maria Pineda Huitron; Esa Vuorinen; Pavel Ernesto Ramí­rez López; Maria Begoña Santillana; Luleå tekniska universitet; []
    Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; Transverse corner cracks; Continuous Casting; Microalloyes steels; Secondary cooling; Cooling curves; Crack susceptibility; Materialteknik; Engineering Materials;

    Sammanfattning : Transverse corner cracks are one of the most common but complex defects formed in microalloyed steels during continuous casting (CC). Such cracks are detrimental because it leads to a loss in productivity with a great impact on environment, energy and economics for several steel making companies all over the world. LÄS MER

  5. 4. High-performance Nickel-based Superalloys for Additive Manufacturing

    Författare :Jinghao Xu; Johan Moverare; Ru Peng; Chinnapat Panwisawas; Linköpings universitet; []
    Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; Nickel-based superalloy; Alloy design; Laser powder bed fusion; Cracking susceptibility; Additive manufacturability; Heat treatment; γ′ precipitate; High-temperature mechanical property; Creep; Oxidation;

    Sammanfattning : Additive manufacturing (AM), e.g., laser powder bed fusion (LPBF) technique, has become a powerful manufacturing process for producing metallic components with the advantages of design freedom, net-shape-forming flexibility, product customization, and reduced lead time to market. LÄS MER

  7. 5. Alloy Design and Characterization of γ′ Strengthened Nickel-based Superalloys for Additive Manufacturing

    Författare :Jinghao Xu; Johan Moverare; Ru Lin Peng; Eric Jägle; Linköpings universitet; []
    Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; Nickel-based superalloy; Alloy design; Laser powder bed fusion; Cracking susceptibility; Additive manufacturability; Heat treatment; γ′ precipitate; High-temperature mechanical property; Creep.;

    Sammanfattning : Nickel-based superalloys, an alloy system bases on nickel as the matrix element with the addition of up to 10 more alloying elements including chromium, aluminum, cobalt, tungsten, molybdenum, titanium, and so on. Through the development and improvement of nickel-based superalloys in the past century, they are well proved to show excellent performance at the elevated service temperature. LÄS MER