  1. 1. Control of Cracking due to Imposed Strains in Concrete Structures

    Författare :Dan Pettersson; Avdelningen för Konstruktionsteknik; []
    Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; hydraulic engineering; Civil engineering; Friction.; Restraint; Shrinkage; Imposed deformations; Minimum reinforcement; Crack widths; Reinforced concrete; Crack development; Crack control; offshore technology; soil mechanics; Väg- och vattenbyggnadsteknik;

    Sammanfattning : This thesis is concerned with crack control due to imposed deformations in concrete structures. The objective of crack control may either be to prevent cracking or to limit the crack widths. The aim here is to increase the knowledge in both fields for some common structures. Five papers are included and the three last concern crack development. LÄS MER

  2. 2. Initiation and early crack growth in VHCF of stainless steels : Experimental and theoretical analysis

    Författare :Muhammad Waqas Tofique; Jens Bergstöm; Nils Hallbäck; Thierry Pallin-Luc; Karlstads universitet; []
    Nyckelord :ENGINEERING AND TECHNOLOGY; TEKNIK OCH TEKNOLOGIER; TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; Very High Cycle Fatigue; Stainless steel; Ultrasonic fatigue testing; Crack initiation; Crystallographic crack growth; Distributed Dislocation Dipole Technique; Closed cracks; Materialteknik; Materials Engineering;

    Sammanfattning : Mechanical fatigue is a failure phenomenon that occurs due to repeated application of mechanical loads. Very High Cycle Fatigue (VHCF) is considered as the domain of fatigue life greater than 10 million load cycles. LÄS MER

  3. 3. Behaviour of fracture process zones in concrete influenced by simultaneously applied normal and shear displacements

    Författare :Manouchehr Hassanzadeh; Avdelningen för Byggnadsmaterial; []
    Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; softening; mixed mode; fictitious crack model; concrete; deformationer; betong; brottmekanik; hållfasthet; brotthållfasthet; spänningar; skjuvspänningar; sprickor; beräkningsmodeller; brottenergi; teori; laboratorieförsök; interlock; crack path; diagonal crack; microcracking; instability; fracture energy; fracture mechanics; shear; tension; process zone;

    Sammanfattning : The thesis deals with the determination of the post peak behaviour of concrete in pure tension, and combined tension (compression) and shear. A test arrangement has been developed in order to determine the post peak behaviour of concrete expressed as stress - displacement curves. LÄS MER

  4. 4. Multistage gearboxes : vibration based quality control

    Författare :Johan Wändell; Hans Bodén; Ulf Carlsson; Kjell Ahlin; KTH; []
    Nyckelord :ENGINEERING AND TECHNOLOGY; TEKNIK OCH TEKNOLOGIER; TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; Acoustics; Akustik;

    Sammanfattning : In this thesis, vibration based techniques for detection of localised surface damages in multistage gearboxes are presented and evaluated. A modern vehicle gearbox is a complex system and the number of potential errors is large. For instance, surface damages can be caused by rough handling during assembly. LÄS MER

  5. 5. A NEW APPROACH TO CRACK CONTROL FOR REINFORCED CONCRETE - An investigation of crack widhts close to the reinforcement and the correlation to service life

    Författare :Kristian Tammo; Avdelningen för Konstruktionsteknik; []
    Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; concrete cover; corrosion; Crack width; steel stress and service life;

    Sammanfattning : One of the most important factors governing durability of concrete structures is reinforcement corrosion, and to prevent degradation associated with it, it is desirable to use large concrete covers. However, if the concrete cover is increased, the majority of design methods will predict that the crack widths at the concrete surface increase significantly. LÄS MER