Sökning: "Cr Evaporation"
Visar resultat 1 - 5 av 23 avhandlingar innehållade orden Cr Evaporation.
1. High Temperature Corrosion Behaviour of Ni-base Alloys and FeCrAl Alloys – The Influence of Water Vapour
Sammanfattning : Electricity production, transportation, and manufacturing industry are some of the largest sources of greenhouse gas emissions. In many cases, these processes are carried out at high temperature and energy efficiency is limited by material degradation, so-called ‘high-temperature corrosion’. LÄS MER
2. Strategies to Mitigate the Degradation of Stainless-Steel Interconnects Used in Solid Oxide Fuel Cells
Sammanfattning : Interconnects are a vital part of solid oxide fuel cells (SOFC), where they electrically connect individual cells to form a fuel cell stack. They are a main contributor to the overall stack cost and the limited life-time of fuel cells, and, therefore, improvements carried out on the interconnect level could further the commercialization of SOFCs. LÄS MER
3. High-temperature corrosion properties of chromia- and alumina-forming alloys
Sammanfattning : Electricity production, transportation, and manufacturing industry are some of the largest sources of greenhouse gas emissions. In many cases, these processes are carried out at high temperature and energy efficiency is limited by material degradation, so-called ‘high-temperature corrosion’. LÄS MER
4. Metallic materials in Solid Oxide Fuel Cells: Oxidation and chromium evaporation properties
Sammanfattning : Solid oxide fuel cells (SOFCs) are high-temperature energy conversion devices which have great potential due to their high efficiency, low operating costs and flexibility in using conventional hydrocarbon based fuels. However, system cost, durability and performance stability in long-term operation are barriers to the widespread commercialization of SOFC technology. LÄS MER
5. The Breakdown of the Protective Oxide on 11% Chromium Steel The Influence of Water Vapour and Gaseous KCl
Sammanfattning : The first part of this thesis is focused on the influence of water vapour on the oxidation of X20 steel (CrMoV 11 1). Three parameters were investigated; pH... LÄS MER