Sökning: "Chloride initiated corrosion"
Visar resultat 1 - 5 av 17 avhandlingar innehållade orden Chloride initiated corrosion.
1. Chloride initiated reinforcement corrosion in marine concrete
Sammanfattning : Factors affecting the total chloride threshold for initiation of pitting corrosion in reinforced concrete were investigated by means of field and laboratory exposure tests. Factors affecting the chloride penetration into concrete were also investigated by means of field tests. The thesis consists of a summary (86 p.) and 11 papers attached. LÄS MER
2. Chloride transport and chloride threshold values : studies on concretes and mortars with Portland cement and limestone blended cement
Sammanfattning : Reinforced concrete is one of the most widely used building materials and if it is properly designed and produced, it is an extremely durable material with a service life up to 100 years. However, under certain environmental conditions the service life of reinforced concrete structures is more limited. LÄS MER
3. Durability of Reinforced Concrete under Impressed Current Cathodic Protection
Sammanfattning : Impressed current cathodic protection (ICCP) and prevention (ICCPre) are reliable and efficient techniques to stop, control and postpone corrosion in reinforced concrete structures. However, the wide application of this technique has been limited by the high cost of the anode system. LÄS MER
4. Chloride Induced Corrosion of Steel Bars in Fibre Reinforced Concrete
Sammanfattning : Chloride-induced corrosion of reinforcement is the most widespread degradation mechanism affecting the durability of reinforced concrete structures. Macro-cracks provide a preferential path for moisture, oxygen and Cl ions to reach the embedded reinforcement, playing a major role in their total transport. LÄS MER
5. Investigations of Chlorine-Induced High Temperature Corrosion of Steels
Sammanfattning : The high corrosivity of the fireside environment in waste and biomass fired boilers is commonly attributed to the presence of chlorine-containing compounds. Chlorine-induced high temperature corrosion is not well understood, however. LÄS MER