  1. 1. Microstructure analysis of wear and fatigue in austempered high-Si steels

    Detta är en avhandling från Luleå : Luleå tekniska universitet

    Författare :Alejandro Leiro; Luleå tekniska universitet.; [2014]
    Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; Engineering Materials; Materialteknik; Konstruktionsmaterial; Engineering Materials; Centre - Centre for High Performance Steel CHS ; Centrumbildning - Centrum för högpresterande stål CHS ;

    Sammanfattning : Research on austempering of high-Si steels has increased over the last years due to their attractive combination of strength and toughness. The presence of over 1.5% of silicon prevents the precipitation of cementite during austempering and the resulting microstructure consists of bainitic ferrite and retained austenite. LÄS MER

  2. 2. High temperature galling influencing parameters and mechanisms

    Detta är en avhandling från Luleå : Luleå tekniska universitet

    Författare :Leonardo Pelcastre; Luleå tekniska universitet.; [2013]
    Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; Machine Elements; Maskinelement; Centre - Centre for High Performance Steel CHS ; Centrumbildning - Centrum för högpresterande stål CHS ;

    Sammanfattning : Damage of forming tools at elevated temperatures is a major problem in metal forming processes such as hot stamping. Of special importance is the occurrence of adhesion and gross material transfer from the work-piece to the tool surface, a phenomenon known as galling. LÄS MER

  3. 3. Wear and fatigue properties of isothermally treated high-Si steels

    Detta är en avhandling från Luleå : Luleå tekniska universitet

    Författare :Alejandro Leiro; Luleå tekniska universitet.; [2012]
    Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; Engineering Materials; Materialteknik; Centre - Centre for High Performance Steel CHS ; Centrumbildning - Centrum för högpresterande stål CHS ;

    Sammanfattning : In recent years steels containing Si contents of 1,5% or more have been isothermally transformed in order to obtain a microstructure consisting of bainitic ferrite laths and retained austenite. The refined microstructure and presence of retained austenite has allowed the manufacture of steels with high tensile strength and considerable elongation. LÄS MER

  4. 4. Hot forming tribology galling of tools and associated problems

    Detta är en avhandling från Luleå : Luleå tekniska universitet

    Författare :Leonardo Pelcastre; Luleå tekniska universitet.; [2011]
    Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; Machine Elements; Maskinelement; Centre - Centre for High Performance Steel CHS ; Centrumbildning - Centrum för högpresterande stål CHS ;

    Sammanfattning : In recent years, the use of ultra high-strength steels (UHSS) as structural reinforcements and in energy-absorbing systems in automobiles has increased rapidly; mainly in view of their favourable strength to weight ratios. However, due to their high strength, the formability of UHSS is poor, thus complex-shaped UHSS components are invariably produced through hot-metal forming processes. LÄS MER

  5. 5. Multiresolution Continuum Theory and Dislocation Density Based Constitutive Relations

    Detta är en avhandling från Luleå tekniska universitet

    Författare :Hao Qin; Luleå tekniska universitet.; [2016]
    Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; Material Mechanics; Materialmekanik; Centre - Centre for High Performance Steel CHS ; Centrumbildning - Centrum för högpresterande stål CHS ;

    Sammanfattning : In classical description, the mechanical state of a material point depends on the variables defined at this point solely. It can integrate and catch some aspects of the material’s microstructure by conventional homogenization method. LÄS MER