Materials and Device Engineering for Efficient and Stable Polymer Solar Cells

Sammanfattning: Polymer solar cells form a promising technology for converting sunlight into electricity, and have reached record efficiencies over 10% and lifetimes of several years. The performance of polymer solar cells depends strongly on the distribution of electron donor and acceptor materials in the active layer. To achieve longer lifetimes, degradation processes in the materials have to be understood. In this thesis, a set of complementary spectroscopy and microscopy techniques, among which soft X-ray techniques have been used to determine the morphology of polymer:fullerene based active layers. We have found that the morphology of TQ1:PC70BM films is strongly influenced by the processing solvent and the use of solvent additives. We have also found, by using soft X-ray techniques, that not only the light-absorbing polymer TQ1, but also the fullerene is susceptible to photo-degradation in air. Moreover, the fullerene degradation is accelerated in the presence of the polymer. Additionally, this thesis addresses the role of the interfacial layers for device performance and stability. The commonly used hole transport material PEDOT:PSS has the advantage of being solution processable at room temperature, but this layer is also known to contribute to the device degradation. We have found that low-temperature processed NiOx is a promising alternative to PEDOT:PSS, leading to improved device performance. Even for encapsulated polymer solar cells, some photo-induced degradation of the electrical performance is observed and is found to depend on the nature of the hole transport material. We found a better initial stability for solar cells with MoO3 hole transport layers than with PEDOT:PSS. In the pursuit of understanding the initial decrease in electrical performance of PEDOT:PSS-based devices, simulations were performed, from which a number of degradation sources could be excluded.