1. AlN Thin Film Electroacoustic Devices
Sammanfattning : Recently, the enormous growth in personal communications systems (PCS), satellite communication and various other forms of wireless data communication has made analogue frequency control a key issue as the operation frequency increases to the low/medium GHz range. Surface acoustic wave (SAW) and bulk acoustic wave (BAW) electroacoustic devices are widely used today in a variety of applications both in consumer electronics as well as in specialized scientific and military equipment where frequency control is required. LÄS MER
2. ZrB2 Thin Films : Growth and Characterization
Sammanfattning : Zirconium diboride, ZrB2, is a ceramic material with bulk properties such as high melting point (3245 °C), high hardness (23 GPa), and low resistivity (~8 μΩcm). Thin film growth of ZrB2 using physical vapor deposition has suffered from problems with films deviating from stoichiometry and with high levels of contaminants, especially high oxygen content. LÄS MER
3. Modelling and Degradation Characteristics of Thin-film CIGS Solar Cells
Sammanfattning : Thin-film solar cells based around the absorber material CuIn1-xGaxSe2 (CIGS) are studied with respect to their stability characteristics, and different ways of modelling device operation are investigated. Two ways of modelling spatial inhomogeneities are detailed, one fully numerical and one hybrid model. LÄS MER
4. Nanocrystalline Tungsten Trioxide Thin Films : Structural, Optical and Electronic Characterization
Sammanfattning : This thesis concerns experimental studies of nanocrystalline tungsten trioxide thin films. Functional properties of WO3 have interesting applications in research areas connected to energy efficiency and green nanotechnology. LÄS MER
5. Atmospheric corrosion of Mg and MgAl alloys – characterization and mechanisms
Sammanfattning : The atmospheric corrosion of Mg and MgAl alloys was investigated. Corrosion tests were performed in the laboratory under controlled environment. CP Mg, AM50 and AZ91 samples were exposed at 95% RH and 22°C in the presence and in the absence of 400 ppm CO2 for 24 h to 672 h. The passive film was characterized by means of XPS, FTIR, AES and XRD. LÄS MER