1. 1. Chloride transport and chloride threshold values : studies on concretes and mortars with Portland cement and limestone blended cement

   Författare :Dimitrios Boubitsas; RISE; []
   Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; Cement; Mortar; Concrete; Corrosion; Reinforcement; Chloride ions;

   Sammanfattning : Reinforced concrete is one of the most widely used building materials and if it is properly designed and produced, it is an extremely durable material with a service life up to 100 years. However, under certain environmental conditions the service life of reinforced concrete structures is more limited. LÄS MER

3. 2. Corrosion of steel bars in fibre reinforced concrete: corrosion mechanisms and structural performance

   Författare :Carlos Gil Berrocal; Chalmers tekniska högskola; []
   Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; residual flexural capacity; chloride-induced corrosion; electrical resistivity; Fibre reinforced concrete; reinforcement bond; durability; cracking;

   Sammanfattning : The viability of employing fibre reinforcement to improve the durability performance of RC structures by delaying and/or reducing rebar corrosion and by mitigating the structural impact of corrosion-induced damage have been investigated. Given the enhanced crack control of FRC, it could be advantageous to use fibres in civil engineering structures to decrease the ingress of corrosion-initiation substances. LÄS MER

4. 3. Chloride initiated reinforcement corrosion in marine concrete

   Författare :Paul Sandberg; Avdelningen för Byggnadsmaterial; []
   Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; w c ratio; cover thickness; chloride penetration; service life prediction; corrosion cells; chloride thresholds; field exposure tests; marine concrete; pozzolans; reinforcement corrosion; chloride binding; Building construction; Byggnadsteknik;

   Sammanfattning : Factors affecting the total chloride threshold for initiation of pitting corrosion in reinforced concrete were investigated by means of field and laboratory exposure tests. Factors affecting the chloride penetration into concrete were also investigated by means of field tests. The thesis consists of a summary (86 p.) and 11 papers attached. LÄS MER

5. 4. Environmental actions on concrete exposed in marine and road environments and its response - Consequences for the initiation of chloride induced reinforcement corrosion

   Författare :Anders Lindvall; Chalmers tekniska högskola; []
   Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; corrosion; de-icing salt; road conditions; marine conditions; service life predictions; reinforcement; chloride; concrete; moisture conditions; environmental actions;

   Sammanfattning : The object of the study presented here has been to describe, further explain and model the influence of the exposure conditions on reinforced concrete structures and the consequences on their expected service life. The focus has been on investigating and quantifying the exposure conditions for structures in marine and road conditions exposed to chloride ions. LÄS MER

7. 5. Natural corrosion in reinforced concrete structures

   Författare :Samanta Robuschi; Chalmers tekniska högskola; []
   Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; Natural corrosion; pitting corrosion; reinforced concrete structures; chloride-induced corrosion.; neutron imaging; anchorage; plain bars; X-rays CT;

   Sammanfattning : Among the threats to the durability of concrete structures, corrosion of the reinforcement bars is undoubtedly the most common one. Corrosion damages impair safety and durability of infrastructure, and assessment of the safety is challenging due to the complex nature of the corrosion process. LÄS MER