Sökning: "high temperature oxidation"

Visar resultat 1 - 5 av 435 avhandlingar innehållade orden high temperature oxidation.

1. 1. On high temperature oxidation resistance : Towards the materials genome of high temperature alloys

   Författare :Samuel Hallström; John Ågren; Roger Reed; KTH; []
   Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; Materials Science and Engineering; Teknisk materialvetenskap;

   Sammanfattning : The efficiency of a heat engine increases with increasing service temperature. This leads to a demand for material that can withstand aggressive environments and sometimes also high load at higher and higher temperature. That is the rationale for the work of this thesis. LÄS MER

3. 2. Performance of High-temperature Coatings : Oxidation and Interdiffusion

   Författare :Xiaoyu Sun; Ru Lin Peng; Johan Moverare; Xin-Hai Li; Lindwall Greta; Linköpings universitet; []
   Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; coating; diffusion; phase transformation; oxidation;

   Sammanfattning : The use of aluminiferous coatings profoundly improves the service life of superalloys but leads to the microstructural degradation of superalloys and thus the loss of mechanical properties. To solve this trade-off, two strategies were employed in this research. LÄS MER

4. 3. High temperature galling : influencing parameters and mechanisms

   Författare :Leonardo Pelcastre; Jens Bergström; Luleå tekniska universitet; []
   Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; Maskinelement; Machine Elements; Centrumbildning - Centrum för högpresterande stål CHS ; Centre - Centre for High Performance Steel CHS ;

   Sammanfattning : Damage of forming tools at elevated temperatures is a major problem in metal forming processes such as hot stamping. Of special importance is the occurrence of adhesion and gross material transfer from the work-piece to the tool surface, a phenomenon known as galling. LÄS MER

5. 4. High Temperature Oxidation and Chlorination of FeCrAl alloys

   Författare :Niklas Israelsson; Chalmers tekniska högskola; []
   Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; KCl; pre-oxidation; FeCrAl; H2O; high-temperature corrosion; kinetics;

   Sammanfattning : AbstractThe constant strive for improved efficiency and lower-cost industrial processes often results in progressively higher temperatures and more aggressive environments. High- temperature corrosion is a well-known problem in biomass- and waste-fired boilers and is one of the obstacles to overcome in achieving a more sustainable society. LÄS MER

7. 5. High-Temperature Corrosion-Fatigue of Cast Alloys for Exhaust Manifolds

   Författare :Shengmei Xiang; Joakim Odqvist; Baohua Zhu; Johan Ahlström; KTH; []
   Nyckelord :TEKNIK OCH TEKNOLOGIER; ENGINEERING AND TECHNOLOGY; High temperature; corrosion fatigue; low-cycle fatigue; cast alloys; high-temperature oxidation; intermetallic phase; Teknisk materialvetenskap; Materials Science and Engineering;

   Sammanfattning : The introduction of gas-driven Otto engine and the corresponding usage of bio-fuels in heavy-duty engines will render the exhaust atmosphere more corrosive and bring a higher working temperature to exhaust manifolds. The current service material, a ferritic ductile cast iron called SiMo51, will soon meet its upper temperature limit set by the ferrite-austenite transformation at 860ºC. LÄS MER